介绍了利用快淬粉制备全密度、高性能、各项异性钕铁硼稀土永磁体的有效方法一热压、热变形方法.成功制备出了磁能积BHm约3.44×105 T·(A/m),剩磁所约1.352 T,矫顽力Hcj约1×106A/m的热变形钕铁硼磁体.利用XRD、VSM、PPMS、SEM等材料表征手段对样品磁性能的各项异性以及取向度进行了分析,并讨论了工艺参数对样品磁性能的影响.
参考文献
| [1] | 周寿增;董清飞.超强永磁体-稀土铁系永磁材料[M].北京:冶金工业出版社,2004 |
| [2] | 解振林,田薇,陈连生.钕铁硼永磁合金烧结过程中的晶粒聚集长大及对磁性能的影响[J].稀有金属材料与工程,2003(04):264-267. |
| [3] | Yutaka Matsuura .[J].Journal of Magnetism and Magnetic Materials,2006,303:344. |
| [4] | Saito T;Fujita M;Kuji T et al.[J].Applied Physics,1998,83(11):6390. |
| [5] | Raja K .[J].Applied Physics,1987,62(03):967. |
| [6] | Kirchnery A;Gronbergery W;Gutfleischz O et al.[J].Applied Physics,1998,31:1660. |
| [7] | Lee R W;Brewer E G;Schaffel N A .[J].IEEE Transactions on Magnetics,1985,21(05):1958. |
| [8] | Lee R W .[J].Applied Physics Letters,1985,46(08):790. |
| [9] | Yong Zhang;Alexander M. Gabay;George C. Hadjipanayis .Microstructure of Nanocomposite R-Fe-B Die-Upset Magnets (R(velence)Pr, Nd) Produced From Mechanically Milled Powders[J].IEEE Transactions on Magnetics,2005(10):3883-3885. |
| [10] | Guruswamy S;Wang Y R;Panchanathan V .[J].Applied Physics,1998,83(11):6393. |
| [11] | Crew D C;Lewis L H;Welch D O et al.[J].Applied Physics,2000,87(09):6570. |
| [12] | Lee D;Hilton J S;Liu S et al.[J].IEEE Transactions on Magnetics,2003,39(05):2947. |
| [13] | Gabay A M;Zhang Y;Hadjipanayis G C .[J].Applied Physics Letters,2004,85(03):446. |
| [14] | Yong Zhang;Alexander M. Gabay;George C. Hadjipanayis .Microstructure of Nanocomposite R-Fe-B Die-Upset Magnets (R(velence)Pr, Nd) Produced From Mechanically Milled Powders[J].IEEE Transactions on Magnetics,2005(10):3883-3885. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%