以偶氮二异丁腈(AIBN)为引发剂,N,N'-亚甲基双丙烯酰胺(BIS)为交联剂,采用自由基聚合法合成了聚乙二醇(PEG)/甲基丙烯酸β-羟乙酯(HEMA)复合凝胶.采用冷冻干燥法制备凝胶支架,结果表明,凝胶支架具有多孔结构,为水分子的进出提供了路径和代谢物通道;随着交联剂用量的增大,水凝胶的平衡含水量降低;凝胶的平衡含水量随着温度的升高而下降,离子强度的增加使水凝胶的溶胀度降低.
参考文献
| [1] | 吴林波,丁建东.组织工程三维多孔支架的制备方法和技术进展[J].功能高分子学报,2003(01):91-96. |
| [2] | Nguyen KT;West JL .Photopolymerizable hydrogels for tissue engineering applications.[J].Biomaterials,2002(22):4307-4314. |
| [3] | Mellott MB;Searcy K;Pishko MV .Release of protein from highly cross-linked hydrogels of poly(ethylene glycol) diacrylate fabricated by UV polymerization.[J].Biomaterials,2001(9):929-941. |
| [4] | Cruise GM;Scharp DS;Hubbell JA .Characterization of permeability and network structure of interfacially photopolymerized poly(ethylene glycol) diacrylate hydrogels.[J].Biomaterials,1998(14):1287-1294. |
| [5] | 石艳丽,张高奇,马敬红,梁伯润.羧甲基纤维素钠/聚（N-异丙基丙烯酰胺）半互穿网络水凝胶的制备及溶胀性能[J].高分子材料科学与工程,2005(05):145-148. |
| [6] | 王云普,袁昆,裴小维.聚N-异丙基丙烯酰胺/纳米SiO2复合水凝胶的合成及溶胀性能[J].高分子学报,2005(04):584-588. |
| [7] | 王建全,吴文辉.不同交联剂对甲基丙烯酸-β-羟乙酯/E-51双甲基丙烯酸酯聚合物水凝胶性能的影响[J].高分子学报,2005(06):868-873. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%