本实验采用乙烯基三甲氧基硅烷钝化镀锌钢板.通过交流阻抗,盐雾和失重实验检测试样的耐腐蚀性能;结果表明试样表面组装一层硅烷膜后耐蚀性大幅度提高,其阻抗值相对空白提高一数量级,抗白锈时间为58h,腐蚀速率降低了近一个数量级.清漆划格实验表明试样再涂装性能良好;原子力检测结果显示硅烷膜致密,起伏较大.初步探讨了硅烷成膜机理.
参考文献
| [1] | 张明宗,管从胜,王威强.有机硅烷偶联剂在金属表面预处理中的应用[J].腐蚀科学与防护技术,2001(02):96-100. |
| [2] | Danqing Zhu;Wim J. van Ooij .Enhanced corrosion resistance of AA 2024-T3 and hot-dip galvanized steel using a mixture of bis-[triethoxysilylpropyl]tetrasulfide and bis-[trimethoxysilylpropyl]amine[J].Electrochimica Acta,2004(7):1113-1125. |
| [3] | Zhu DQ.;van Ooij WJ. .Corrosion protection of metals by water-based silane mixtures of bis-[trimethoxysilylpropyl]amine and vinyltriacetoxysilane [Review][J].Progress in Organic Coatings: An International Review Journal,2004(1):42-53. |
| [4] | Socha RP;Pommier N;Fransaer J .Effect of deposition conditions on the formation of silica-silicate thin films[J].Surface & Coatings Technology,2007(12):5960-5966. |
| [5] | 胡吉明,刘倞,张金涛,张鉴清,曹楚南.铝合金表面BTSE硅烷化处理研究[J].金属学报,2004(11):1189-1194. |
| [6] | 胡吉明,刘倞,张鉴清,曹楚南.LY12铝合金表面电化学沉积制备DTMS硅烷膜及其耐蚀性研究[J].高等学校化学学报,2006(06):1121-1125. |
| [7] | 王雪明,李爱菊,李国丽,管从胜.硅烷偶联剂在防腐涂层金属预处理中的应用研究[J].材料科学与工程学报,2005(01):146-150. |
| [8] | 曾凡辉,姜其斌,陈宪宏.硅烷偶联剂WD-60在环氧防腐涂料中的应用[J].涂料工业,2007(01):27-28,32. |
| [9] | 徐溢,王楠,张小凤,金洋华.直接用作金属表面新型防护涂层的硅烷偶联剂水解效果分析[J].腐蚀与防护,2000(04):157-159. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%