Carbide formation in austempered ductile iron (ADI) alloyed with Ni and Cu has been studied by use of TEM. The results show that η carbide precipitates in the bainitic ferrite when austempered at 350℃.for 6h, but no carbide was found at the austenite/.ferrite interfaces. When austempered at 300℃, two kinds of. s carbides appear in the bainitic ferrite when austempering time reached I h, and X carbide also precipitates at the austenite /ferrite interfaces when austempering time was extended up to 6h. The bainitic. ferrite and the retained austenite follow the Nishiyama- Wasserman relationship,
参考文献
| [1] | WilkinsonG,GrupdeC．Proceedingsofthe2ndinternationalConferenceonADI,Michigan,1986,3492HardingRA．OpeninguptheMarketforADI,IBFAnnualconf,19923HayrymenKL,FaubertGP,MooreDJ,RundmanKB．TransAFS,1989:7474GrechM．PhD．Diss．,UniversityofBirmingham,UK,19895RundmanK,RounsT,DubenskyW,MooreD．Proceedingsofthe2ndInternationalConferenceonADI,Michigan,1986:1576SidjaninL,SmallmanRE,BoutorabiSM．MaterSciTechnol,inpress7SidjaninL,SmallmanRE．MaterSciTechnol,1992:12(8):10958FanZK．SmallmanRE．ScrMetallMater,1994:31(2):1379DirandM,AfqirL．ActaMetall,1983:31:1089 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%