选择AZ91D镁合金为实验材料,在通过正交实验优化镁合金表面植酸转化膜成膜工艺的基础上,利用扫描电镜、能谱分析、点蚀实验和电化学测量等分析手段研究了植酸浓度对植酸转化膜表面形貌、表面成分及其耐蚀性的影响.结果表明植酸转化膜主要由Mg、A1、O、P和C元素组成,其中Mg元素含量随着植酸浓度的增大而减小,而P元素含量随着植酸浓度的增大逐渐增大.镁合金表面植酸转化膜的表层厚度和表面裂纹宽度随植酸浓度的增大而增大,且转化膜表层中裂纹的存在及裂纹的尺寸大小不影响转化膜的耐蚀性.转化膜化学成分和结构的不同主要是影响合金电极阳极溶解反应的动力学机构,从而使合金的阳极溶解电流密度降低,对阴极反应的动力学机构影响不大.
参考文献
| [1] | Zhao M;Wu SS;Luo JR;Fukuda Y;Nakae H .A chromium-free conversion coating of magnesium alloy by a phosphate-permanganate solution[J].Surface & Coatings Technology,2006(18/19):5407-5412. |
| [2] | Tian XB;Wei CB;Yang SQ;Fu RKY;Chu PK .Corrosion resistance improvement of magnesium alloy using nitrogen plasma ion implantation[J].Surface & Coatings Technology,2005(1/3):454-458. |
| [3] | Song G L;Jhon D S .[J].Corrosion Science,2004,46(06):1381. |
| [4] | 曾荣昌,柯伟,徐永波,韩恩厚,朱自勇.Mg合金的最新发展及应用前景[J].金属学报,2001(07):673-685. |
| [5] | Ambat R.;Zhou W. .Electroless nickel-plating on AZ91D magnesium alloy: effect of substrate microstructure and plating parameters[J].Surface & Coatings Technology,2004(2/3):124-134. |
| [6] | 高瑾,涂运骅,李久青.镁合金涂装保护体系失效特性及铬酸盐转化膜的影响[J].腐蚀科学与防护技术,2005(03):169-171. |
| [7] | Eppensteiner F W;Jenkins M R .[J].Metal Finishing,2002,100(01):479-491. |
| [8] | Nan J Y;Li C F;Yu B L .[J].Metallurgical and Materials Transactions,2008,39(03):703-715. |
| [9] | Niu LY;Jiang ZH;Li GY;Gu CD;Lian JS .A study and application of zinc phosphate coating on AZ91D magnesium alloy[J].Surface & Coatings Technology,2006(9):3021-3026. |
| [10] | Cui X F;Li Q F;Li Y.[J].Applied Surface Science,2008(255):2098-2103. |
| [11] | Liu JR;Guo YN;Huang WD .Study on the corrosion resistance of phytic acid conversion coating for magnesium alloys[J].Surface & Coatings Technology,2006(3/4):1536-1541. |
| [12] | Zhang S Y;Li Q;Chen B.[J].Electrochimica Acta,2009 |
| [13] | Dorscha J A;Cooka A;Kevin A .[J].Phytochemistry,2003,62:691-706. |
| [14] | 霍宏伟,李瑛,王福会.化学转化膜上沉积镍对镁合金耐腐蚀性能的影响[J].中国有色金属学报,2004(02):267-272. |
| [15] | 张华云,李华伦,郭伊娜.镁合金化学转化膜的耐腐蚀性研究[J].材料保护,2007(01):10-12. |
| [16] | Zhang R F;Zhang S F;Duo S W .[J].Applied Surface Science,2009,255:7893-7897. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%