利用MoSi2,Al,C之间的原位反应无压烧结制备了Mo(Si1-x,Alx)2-SiC复合材料.随着烧结温度从1400℃升高到1650℃,MoSi2相消失,反应产物为Mo(Si,Al)2和SiC及Mo5Si3C相.由于固溶体及Nowotny(Mo5Si3C)相的形成,使得原位反应中化学计量法则变得困难.原位生成的SiC相随着温度的升高由颗粒状变为晶须状,并由于它的强韧化作用使得复相材料的性能较单相材料成倍提高.
参考文献
| [1] | 江莞,赵世柯,王刚.二硅化钼材料的研究现状及应用前景[J].无机材料学报,2001(04):577-585. |
| [2] | Vasudevan A K;Petrovic J J.[J].Materials Science and Engineering(01) |
| [3] | 张小立,吕振林,金志浩.无压反应烧结MoSi2-SiCp复相材料的制备与性能[J].稀有金属材料与工程,2003(12):1037-1040. |
| [4] | Petrovic J J;Vasudevan A K.[J].Materials Science and Engineering A(01) |
| [5] | Stoloff N S.[J].Materials Science and Engineering A:169. |
| [6] | Jayashankar J S;Ross E N.[J].Materials Science and Engineering A:485. |
| [7] | Petrovic J J.[J].Materials Science and Engineering A:31. |
| [8] | Liu Y Q;Shao G;Tsaliropoulos P.[J].INTERMETALLICS,2001:125. |
| [9] | Stergiou A.[J].INTERMETALLICS,1997:69. |
| [10] | Zhang G J.[J].Journal of Materials Science,1999:593. |
| [11] | Shobu K.[J].Journal of the American Ceramic Society:544. |
| [12] | Zhang G J.[J].Journal of Materials Science,2000:4729. |
| [13] | Krishnarao R V.[J].Journal of Materials Research,1997(12):3322. |
| [14] | Suzuki Y;Nuhara K.[J].INTERMETALLICS,1998:7. |
| [15] | Idem.[J].Key Engineering Materials:271. |
| [16] | 武七德,鄢永高,赵修建,郭兵健,李美娟,刘小磐.纯碳坯渗硅制备反应烧结碳化硅的研究[J].武汉理工大学学报,2003(06):1-3. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%