类金刚石膜作为新型的生物材料得到了广泛的关注.本实验制备的薄膜为典型的类金刚石膜,膜层比较致密、均匀和光滑.膜层硬度随离子束能量变化,在束电源为750V附近出现峰值,硬度达到了15GPa,该膜的摩擦系数为0.124.在Troyde's模拟体液中的电化学分析表明,类金刚石膜显著提高了TiNi合金表面抗点蚀能力.
参考文献
| [1] | Dowling D P;kola P V;Donedy K.[J].Diamond and Related Materials,1997:390. |
| [2] | Grill A.[J].Surface and Coatings Technology:507. |
| [3] | Tallant D R;Parmeter J E;Siegel M P.[J].Diamond and Related Materials,1995:191. |
| [4] | Grischke M;Bewilogua K;Trojan K.[J].Surface and Coatings Technology:739. |
| [5] | De S I;Szilard M;Yanming H.[J].Invasive Cardiol:389-394. |
| [6] | 程宇航;吴一平.[J].功能材料,1998(01):54-57. |
| [7] | 黄立业,徐可为,杨生荣,刘维民.生物医用类金刚石薄膜的力学性能评价[J].稀有金属材料与工程,2001(05):357-360. |
| [8] | 周燕芳,钟辉.锂离子电池正极材料的研究进展[J].材料开发与应用,2003(02):34-38,42. |
| [9] | 刘成龙,杨大智,赵红.316L不锈钢表面液相沉积TiO2薄膜的耐蚀性研究[J].功能材料,2003(05):600-602. |
| [10] | Paterson M J.[J].Diamond and Related Materials,1996:1407. |
| [11] | Nicklow R;Wakabayashi N;Smith H G.[J].PHYSICAL REVIEW B,1972:4951-4959. |
| [12] | Tamor M A;Vassell W C.[J].Journal of Applied Physiology:3823. |
| [13] | Prawer S;Nugent K W;Lifshitz Y.[J].Diamond and Related Materials,1996:433-437. |
| [14] | 刘敬肖 .316L不锈钢和NiTi合金表面薄膜的制备、结构及其生物相容性研究[D].大连理工大学,2001. |
| [15] | Lifshitz Y.[J].PHYSICAL REVIEW LETTERS,1987(01):75. |
| [16] | Weissmante C et al.[J].THIN SOLID FILMS,1983,100:383. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%