Long Lasting Phosphorescence in Eu2+ and Ce3+ Co-Doped Strontium Borate Glasses

稀土学报(英文版), 2006, 24(z2): 196-198.

^1, , ^2, , ^3,

1.Key Laboratory of Rare Earth Chemistry and Physics, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China;State Key Laboratory of Optoelectronic Materials and Technologies, School of Chemistry and Chemical Engineering, Sun Yat-Sen University, Guangzhou 510275, China

2.Key Laboratory of Rare Earth Chemistry and Physics, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China

3.Key Laboratory of Rare Earth Chemistry and Physics, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China;State Key Laboratory of Optoelectronic Materials and Technologies, School of Chemistry and Chemical Engineering, Sun Yat-Sen University, Guangzhou 510275, China

基金项目: 吉林省重点科研项目(20020601)

Long Lasting Phosphorescence in Eu2+ and Ce3+ Co-Doped Strontium Borate Glasses

Keywords： long lasting phosphorescence

Long lasting phosphorescence (LLP) was observed in Eu2+, Ce3+ co-doped strontium borate glasses prepared under the reducing atmosphere due to the emission of both Eu2+ and Ce3+. The methods of photoluminescence, thermoluminescence and phosphorescence were used to study the samples, and possible mechanism was suggested. The co-doping of Ce3+ ions poisoned the phosphorescence emission of Eu2+ because of the competition to obtain the trapped electron. The phosphorescence of Ce3+ in the sample decays more quickly than that of Eu2+, which is suggested for the reason that the emission energy of Ce3+ is higher or the distance between Ce3+ and electron traps of the glasses is longer.

参考文献

[1]	Qiu JR.;Hirao K. .Long lasting phosphorescence in Eu2+-doped calcium aluminoborate glasses[J].Solid State Communications,1998(12):795-798.
[2]	Qiu J.;Tanaka K.;Shimizugawa Y.;Hirao K.;Kawasaki M. .Phenomenon and mechanism of long-lasting phosphorescence in Eu2+-doped aluminosilicate glasses[J].The journal of physics and chemistry of solids,1998(9):1521-1525.
[3]	Lin Yuanhua;Tang Zilong;Zhang Zhongtai et al.Preparation and properties of photoluminescent rare earth doped SrO-MgO-B2O3-SiO2 glass[J].Materials Science and Engineering,2001,B86:79.
[4]	Kim J H;Holloway P H .Room-temperature photoluminescence and electroluminescence properties of sputter-grown gallium nitride doped with europium[J].Journal of Applied Physics,2004,95:4787.
[5]	Tian Zifeng;Liang Hongbin;Lin Huihong et al.Luminescence of NaGdFPO4:Ln3+ after VUV excitation:A comparison with GdPO4:Ln3+ (Ln=Ce,Tb)[J].Journal of Solid State Chemistry,2006,179:1356.
[6]	Zhang T;Su Q .Rare-earth materials for use in the dark[J].J of the SID,2000,8:27.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Long Lasting Phosphorescence in Eu2+ and Ce3+ Co-Doped Strontium Borate Glasses

参考文献