采用工程法和近似塑性条件dσr=dσz, 并将接触面假设为混合摩擦条件, 对液相线半连续铸造法获得的7075铝合金半固态浆料的触变成型力进行了计算. 计算结果表明: 在变形的开始阶段, 成型力为32kN; 在变形的终了阶段, 成型力为667.09kN, 与实测结果721kN基本符合.
参考文献
| [1] | Irkwood D H;Kapranos P .Semi-solid processing of alloy[J].Metals and Materials,1988,11(02):16-20. |
| [2] | Flemings M C;Piek R G;Young K P .The theology of a partially solid alloy[J].Metallurgical and Materials Transactions,1972,17(03):1925-1932. |
| [3] | Fleming M C .Behavior of metal alloys in the semi-solid state[J].Metallurgical and Materials Transactions,1991,22(06):269-291. |
| [4] | Chiarmetta G.Thixoforming of automobile components[A].Shetlied:The University of Sheffield,1996:204-207. |
| [5] | Masayuki N;Yuh S;Flemings M C .Semi-solid processing of copper alloys for electric motor components[J].International Journal of Mechanical Sciences,1990,30(01):27-33. |
| [6] | Lu G;Cui J;Dong J.Continuous casting of Al alloy 7075 for semi-solid forming[A].Italy,Iurin:Edimet Spa-via Corfu,2000:373-377. |
| [7] | 崔建忠,路贵民,刘丹.半固态浆制备技术的新进展[J].哈尔滨工业大学学报,2000(04):110. |
| [8] | 刘丹,崔建忠,夏克农.液相线铸造铝合金2618显微组织[J].东北大学学报（自然科学版）,1999(02):173-176. |
| [9] | 路贵民,董杰,崔建忠.7075合金液相线半连续铸造与二次加热的合金组织[J].中国有色金属学报,2001(02):211-2156. |
| [10] | 赵德文;刘湘华;王国栋.圆形平冲头压缩半无限体的上界理论解法[J].东北大学学报(自然科学版),1996(01):69-74. |
| [11] | 赵德文;王国栋.工程法解析平冲头压入半无限体[J].东北大学学报(自然科学版),1992(04):369. |
| [12] | 刘丹 .铝合金液相线铸造工艺及理论研究[D].沈阳:东北大学,1999. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%