采用二步重熔法制备不同Gd含量的Pb-Gd合金材料，采用抗拉强度测试、阳极失重法研究Gd对Pb-Gd合金力学性能和耐腐蚀性能的影响，并利用CV(循环伏安曲线)和XRD分析研究Gd含量对Pb-Gd合金阳极电化学性能及物相组成的影响。结果表明：合金抗拉强度随Gd含量的增大而增大，当Gd含量达到2.0%(质量分数)时，合金抗拉强度为19.1 MPa，比纯Pb的提高69.0%；添加Gd没有影响阳极表面氧化膜物相的基本组成，阳极的表面氧化膜主要由β-PbO 2和PbO组成。稀土元素Gd能降低合金电极阳极稳定电位，且电位值随稀土元素含量的增加而减小。
The Pb-Gd alloy anodes with different Gd contents were prepared by two stage remelting method. The effects of Gd contents on the tensile strength and corrosion resistance of Pb-Gd alloy anodes were examined by mechanics performance and mass-loss method. The cyclic voltammetry curve (CV) and XRD were used to study the electrochemical behaviour and phase composition of the Pb-Gd alloy anode . The result show that the tensile strength of Pb-Gd alloy anode increase with increasing the Gd content, when Gd content is 2.0% (mass fraction), the tensile strength of Pb-Gd alloy anode reaches 19.1 MPa which increases by 69.0% comparing with that of pure Pb anode. Addition of Gd can not change the surface film of lead anode, its mainly composes ofβ-PbO 2 and PbO. But addition of Gd can reduce the anode steady potential, and the potential value decreases with increasing the rare earth metal content.
参考文献
| [1] | Ivanov I.;Stefanov Y. .Insoluble anodes used in hydrometallurgy Part I. Corrosion resistance of lead and lead alloy anodes[J].Hydrometallurgy,2000(2):109-124. |
| [2] | Ivanov I.;Stefanov Y. .Insoluble anodes used in hydrometallurgy Part II. Anodic behaviour of lead and lead-alloy anodes[J].Hydrometallurgy,2000(2):125-139. |
| [3] | 于枭影,李艳红,蒋良兴,赖延清,李劼,刘业翔.多孔Pb合金阳极在电积制备铜粉中的应用特性[J].中国有色金属学报,2013(05):1323-1330. |
| [4] | 衷水平,LAI Yan-qing,蒋良兴,TIAN Zhong-liang,李劼,LIU Ye-xiang.锌电积用Pb-Ag-Ca-Sr四元合金阳极的阳极极化行为[J].中国有色金属学报,2008(07):1342-1346. |
| [5] | LAI Yan-qing;JIANG Liang-xing;LI Jie;ZHONG Shui-ping LIU Ye-xiang .A novel porous Pb-Ag anode for energy-saving in zinc electro-winning:Part Ⅰ:Laboratory preparation and properties[J].HYDROMETALLURGY,2010,102(1/4):73-80. |
| [6] | HRUSSANOVA A;MIRKOVA L;DOBREV TS;VASILEV S .Influence of temperature and current density on oxygen overpotential and corrosion rate of Pb-Co 3 O 4,Pb-Ca-Sn and Pb-Sb anodes for copper electrowinning:Part Ⅰ[J].HYDROMETALLURGY,2004,72(3/4):205-213. |
| [7] | 杨海涛,陈步明,郭忠诚.铅基合金阳极在有色金属湿法冶炼中的研究与发展[J].中国有色冶金,2012(02):20-24,7. |
| [8] | 张文达,杨晶,刘云,党惊知,徐宏.稀土Y对AlSi7Cu2Mg合金高温性能的影响[J].中国有色金属学报,2013(07):1855-1860. |
| [9] | 李鑫,王涛,魏绪钧,徐秀芝.稀土在铅基合金中的应用[J].有色金属,2003(02):15-17. |
| [10] | 洪波,蒋良兴,吕晓军,倪恒发,赖延清,李劼,刘业翔.Nd对锌电积用Pb-Ag合金阳极性能的影响[J].中国有色金属学报,2012(04):1126-1131. |
| [11] | 杨春晓,张新华,周彦葆,柳厚田.Pb-Gd合金在硫酸溶液中生长的阳极Pb（Ⅱ）膜的阻抗的研究[J].复旦学报(自然科学版),2004(04):584-588. |
| [12] | 刘芳清,张新华,马敏,柳厚田.镨和钕对硫酸溶液中铅阳极膜阻抗特性的影响[J].复旦学报（自然科学版）,2008(05):659-662. |
| [13] | 李党国,周根树,姚靓,郑茂盛.铅铈和铅钙锡合金阳极腐蚀膜的性能研究[J].化学学报,2007(07):584-588. |
| [14] | Yan-Bao Zhou;Chun-Xiao Yang;Wei-Fang Zhou .Comparison of Pb-Sm-Sn and Pb-Ca-Sn alloys for the positive grids in a lead acid battery[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2004(1/2):108-111. |
| [15] | 刘生发,王慧源,康柳根,黄尚宇,徐萍.钕对AZ91镁合金铸态组织的影响[J].中国有色金属学报,2006(03):464-469. |
| [16] | H. Li;W.X. Guo;H.Y. Chen;D.E. Finlow;H.W. Zhou;C.L. Dou;G.M. Xiao;S.G. Peng;W.W. Wei;H. Wang .Study on the microstructure and electrochemical properties of lead-calcium-tin-aluminum alloys[J].Journal of Power Sources,2009(1):111-118. |
| [17] | 王志峰,赵维民,崔妍,范生磊.稀土元素Ce、Dy、Nd对Mg-Zn-Y基准晶合金显微组织的影响[J].中国铸造装备与技术,2011(03):1-3. |
| [18] | 魏杰,赵力,孙芬莉,杨红,褚德威.含铈和钇的铅酸蓄电池板栅合金添加剂[J].中国有色金属学报,2003(02):497-501. |
| [19] | 柳厚田,张新华,杨炯,杨春晓,周伟舫.铈降低在硫酸溶液中生长的阳极Pb（Ⅱ）氧化物膜的电阻的研究[J].化学学报,2002(04):643-646. |
| [20] | 柳厚田,杨春晓,梁海河,杨炯,周伟舫.铅镧和铅钐合金在硫酸溶液中生长的阳极膜性质的研究[J].电化学,2001(04):439-444. |
| [21] | LAITINEN T;SUNDHOLM G;VILHUNEN J K .Comments on sample treatment in the X-ray diffraction analysis of the oxidation products of lead[J].Journal of Power Sources,1990,32:71-80. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%