采用高温固相熔融法在弱还原气氛下制备了Ce3+离子掺杂的Y2O3-A12O3-SiO2(SAY)系基础玻璃,并在1250℃~1300℃热处理一定时间制备了晶相为YAG的黄色微晶玻璃。通过XRD、SEM研究了微晶玻璃的结构及相组成;激发和发射光谱分析了Ce3+离子在玻璃及微晶玻璃不同基质中的发光特性,以及Al2O3/Y2O3摩尔比对微晶玻璃样品发光性能的影响。结果表明:基础玻璃经热处理能得到Ce-YAG微晶玻璃,晶粒大小在80~120nm范围内,晶粒发育良好。该微晶玻璃样品能被450nm有效激发,并在530nm处有宽带发射峰,归属于Ce3+的5d-4f(2F2/7)。该微晶玻璃在LED照明领域中有很大的应用开发价值。Al2O3和Y2O3的摩尔含量变化对微晶玻璃发光性能有较大影响,在Al2O3/Y2O3的摩尔比为1.5时,样品的发光性能最佳。
Ce3+ doped Y2O3-Al2O3-SiO2 (SAY) glass was synthesized by high temperature solid-state melting method under weak reducing atmosphere, and yellow YAG glass-ceramic was obtained after being heat treated at 1250℃ 1300℃. By using X-ray diffractometry (XRD) and scanning electron microscopy (SEM), we studied the crystalline phase structure of the glass-ceramic. The luminescence characteristics of Ce3+ ion in different matrixes of glass and glass-ceramic samples were studied by the excitation and emission spectroscopy, and we also studied the influence of Al2O3/Y2 O3 on the luminescence properties. The results show that we can obtain the Ce-YAG glas-ceramics after heat treating the as-made glasses, and the grain size of the Ce-YAG phase is between 80-120nm with well-developed grains. The glass ceramics can emit yellow fluorescence centered at 530nm with a broad emission spectrum under the excitation at 450nm, which attributes to the energy transfer 5d-4f (2 F2/7 ) of the Ce^3+ , and indicates that it has a great value in application and development in the field of LED lighting. The molar ratio of Al2O3/Y2O3 has a great effect on the luminescence properties of the as-made glass-ceramics. When the A12O3/Y2O3 equals to1.5, the sample has the excellent luminescent performance.
参考文献
[1] | Nakamura S;Fasol G.The blue laser diode:GaN Based LightEmitters and Lasers[M].Beilin:Springer-Verlag,1997 |
[2] | 崔元日,潘苏予.第四代照明光源--白光LED[J].灯与照明,2004(02):31-34. |
[3] | Yi Zheng;Alexis Clare .Blue light excited glasses for white lightillumination[J].Advances in Photonic Materials and Devices,2005,163:99-105. |
[4] | Shimizu .Development of White LED light source[J].RareEarth,2002,150:40. |
[5] | CARL Z.Advances in LED packaging and thermal managementmaterials[J].Light Emitting Diodes,2008:1-7. |
[6] | FUJITA S;YOSH I S;SAKAMOTO A;et a1.YAG glass-ceramic phosphor for white LED(I):background anddevelopment[A].BeUingham,WA,2005:594111-5941-7. |
[7] | S.Tanabe;S.Fujita;A.Sakamoto;S.Yamamoto .Glassceramics for solid-state lighting[J].British Ceramic Transactions,2006,173:19-25. |
[8] | S.Fujita;Y.Umayahara;S.Tanabe .Influence of lightscattering on luminous efficacy in Ce:YAG glass-ceramicphosphor[J].Journal of the Ceramic Society of Japan,2010,118(02):128-131. |
[9] | 宋国华,缪建文,徐淑武,纪宪明.YAG:Ce~(3+)玻璃陶瓷白光LED的发光特性[J].光电子·激光,2010(12):1785-1789. |
[10] | 刘树杰,关荣锋.用于白光LED的掺杂Ce-YAG荧光玻璃的研制[J].电子元件与材料,2007(12):8-9,20. |
[11] | Jacobs R;Krupke;WF'Weber M .Measurement of excited stateabsorption loss Ce3+in Y3Al5O12and implications for tunable 5d-4f rare earth lasers[J].Applied Physics Letters,1978,33(02):409. |
[12] | 李建宇.稀土发光材料及其应用[M].北京:化学工业出版社,2003:154-156. |
[13] | J.H.Fisher;W.A.Hollerman;G.A.Shelby;et a1 .Spectroscopic analysis of proton induced fluorescence fromcerium doped yttrium aluminum garnet[J].Nuclear Instrumentsand Methods in Physics Research Section B:Beam Interactionswith Materials and Atoms,1993,80-81(02):1207-1209. |
[14] | Blasse G;Bril A .Investigation of some Ce3+-activatedphosphors[J].Journal of Chemical Physics,1967,12(47):5139-5145. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%