通过铜模吸铸法制备亚快速凝固Cu-15Al-4Fe合金棒材.利用光学显微镜、扫描电镜、能谱仪、X射线衍射、静态浸泡和电化学实验等,研究了合金的组织形貌、成分分布、相组成及耐腐蚀性能.结果表明,亚快速凝固Cu-15Al-4Fe合金呈柱状晶组织,主要由先共析γ2相和(α+γ2)共析体组成.合金在3.5％NaCl和5.0％H2SO4腐蚀液中主要发生脱铝脱铁选择性腐蚀.与5.0％H2SO4溶液相比,合金在3.5％NaCl溶液中存在明显的钝化现象,耐蚀性较高.
参考文献
| [1] | Han Z,Zhao H.Effect of β martensite transformation on dealuminification behavior of Cu-9Al-2Mn alloy in a marine environment[J].Mater.Sci.Eng.,2003,A345(1-2):8 |
| [2] | Li W S,Wang Z P,Lu Y,et al.Mechanical and tribological properties of a novel aluminum bronze material for drawing dies[J].Wear,2006,261(2):155 |
| [3] | Heide E,Stam E D,Giraud H,et al.Wear of aluminium bronze in sliding contact with lubricated stainless steel sheet material[J].Wear,2006,261(1):68 |
| [4] | Li Y Y,Tungwai L N,Wei X.Mechanical,friction and wear behaviors of a novel high-strength wear-resisting aluminum bronze[J].Wear,1996,197(1-2):130 |
| [5] | 于辉,董飒英,黄国胜等.铝青铜在315 ％NaCl溶液中的脱成份腐蚀行为[J].中国腐蚀与防护学报,2003,23(6):345-349 |
| [6] | 韩忠,江伟明,林海潮等.海水管路系统中铝青铜腐蚀行为的研究[J].中国腐蚀与防护学报,2000,20(3):188-192 |
| [7] | 路阳,张鹤,苏义祥等.铁对铸态高铝青铜组织和性能的影响[J].铸造,2007,56(2):199 |
| [8] | 路阳,李振,李文生等.微量元素Fe对高铝铜合金腐蚀行为的影响[J].热加工工艺,2008,37(10):33 |
| [9] | 张鹤.铁对高铝青铜组织和摩擦磨损性能的影响[D].甘肃:兰州理工大学,2007 |
| [10] | 王凤平,康万利,敬和民.腐蚀电化学原理、方法及应用[M].北京:化学工业出版社,2008 |
| [11] | Li W S,WANG Z P,LU Y,et al.Corrosion and wear behaviors of Al-bronzes in 5.0％ H2SO4 solution[J].Trans.Nonferrous Met.Soc.China.,2009,19(2):311 |
| [12] | 李文生,路阳,王智平等.Cu-14Al-X合金在5.0％H2SO4溶液中的腐蚀行为[J].中国有色金属学报,2007,17(6):951 |
| [13] | 李文生,王智平,路阳等.高铝青铜Cu-14Al-X合金在3.5％NaCl溶液中的腐蚀行为[J].中国有色金属学报,2006,16(3):511 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%