采用水热法在双温区加热炉中以Z-切向晶片为籽晶生长了掺铌KTiOPO4单晶(Nb∶ KTP),得到尺寸为24.7mm×14.7 mm× 42.6 mm的透明晶体.研究了Nb∶ KTP水热条件下的生长习性和宏观、微观缺陷,通过其与纯KTP的透过谱的对比,对晶体质量进行了初步评估,与高质量的水热高抗灰迹KTP晶体有相当的质量.
参考文献
| [1] | Cheng L T;Cheng L K;Harlow R L et al.Straight Produce Blue Light Using Bulk Niobium Doped KTiOPO4 Crystal[J].Applied Physics Letters,1994,64(02):155. |
| [2] | Zhang CL;Huang LX;Zhou WN;Zhang G;Hou HD;Ruan QF;Lei W;Qin SJ;Lu FH;Zuo YB .Growth of KTP crystals with high damage threshold by hydrothermal method[J].Journal of Crystal Growth,2006(2):364-367. |
| [3] | Zhang, CL;Hu, ZG;Huang, LX;Zhou, WN;Lue, Z;Zhang, G;Liu, YC;Zou, YB;Lu, FH;Hou, HD .Growth and optical properties of bulk KTP crystals by hydrothermal method[J].Journal of Crystal Growth,2008(7/9):2010-2014. |
| [4] | 黄凌雄,霍汉德,张戈,张昌龙,黄呈辉,周卫宁,魏勇.KTP晶体的水热法生长及其光学性能的测量[J].人工晶体学报,2007(02):256-259. |
| [5] | 魏景谦.掺铌KTP晶体的生长和性质研究[J].人工晶体学报,1995(04):291. |
| [6] | 张德颖,沈鸿元,刘文,张国芳,陈文志,张戈,曾瑞荣,黄呈辉,林文雄.Nb∶KTiOPO4晶体的生长和倍频性能[J].人工晶体学报,1999(03):298-302. |
| [7] | 金成国,李珍,张昌龙,鲁立强,李艳芹,马兰.水热法和熔盐法生长的Nb： KTP晶体成分和结构研究[J].人工晶体学报,2009(04):826-830. |
| [8] | 金成国,李珍,张昌龙,黄凌雄,谢浩.Nb∶KTP晶体成分、结构和拉曼光谱的研究[J].人工晶体学报,2011(06):1376-1381. |
| [9] | Growth of KTP crystals with large {001} facets[J].Journal of Crystal Growth,2010(8):p.1055. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%