以锂辉石为原材料,在简化石灰石法的基础上,对抑制碱-集料反应用LiNO3的制备工艺和工艺参数进行了研究,并对抑制效果进行了评价.合成试验表明:在锂辉石∶碳酸钙=1∶2.7、焙烧温度为1100℃、焙烧时间为60 min和浸出时间为120 min的工艺参数情况下,Li的溶出率可高达88.45%;抑制试验表明:在80℃养护条件下,碱含量为2.5%和Li/Na摩尔比为0.74时,掺加试验室合成的硝酸锂可取得与硝酸锂分析纯较为接近的抑制效果,均可使3种集料成型砂浆试件90d时的膨胀率小于0.1%.
参考文献
| [1] | McCoy W J;Caldwell A G .New approach to inhibiting alkali-aggregate expansion[J].J Ame Concrete Institute,1951,22(09):693. |
| [2] | Stark D C.Lithium salt admixtures-an alternative method to prevent expansive alkali-silica reactivity[A].Concrete Society of U.K,London,1996:1017. |
| [3] | Lane D S .Laboratory investigation of lithium-bearing compounds for use in concrete[Virginia Transportation Research Council,VTRC 02-R16][R].,2002. |
| [4] | Wang H;Stokes D B.Compatibility of lithium-based admixtures with other concrete admixtures[A].CSIRO Division of Building Construction and Engineering Melbourne,Australia,1996:884. |
| [5] | Diamond S .Unique response of LiNC3 as an alkali silica reaction preventive admixture[J].Cement and Concrete Research,1999,29:1271. |
| [6] | 冉建中.采用锂云母-石灰石法生产锂盐的节能途径及效果[J].江西有色金属,1995(01):36. |
| [7] | 马斌霞.硫酸法生产碳酸锂工艺过程中酸熟料中和机理探讨[J].新疆有色金属,2000(04):31. |
| [8] | 周小菊;彭吉中;马声威 等.四川锂辉石生产单水氢氧化锂烧结条件研究[J].西南民族学院学报(自然科学版),1995,21(03):299. |
| [9] | 李天伶.β-锂辉石的晶体化学性质及其低热膨胀性的结构解释[J].硅酸盐通报,1995(02):27. |
| [10] | 施洪钧,赵玉珍.ICP-AES法同时测定氯化锂和氢氧化锂中七种杂质元素[J].光谱实验室,1998(03):0. |
| [11] | 苏亚勤,章新泉,易永,李翔,刘永林.电感耦合等离子体质谱法测定高纯碳酸锂中的杂质元素[J].江西化工,2004(04):145-147. |
| [12] | CECS 48:1993.CECS 48:1993.砂、石碱活性快速试验方法[S].北京:中国建设标准化协会,1995. |