利用固相反应烧结法制备了层状钙钛矿锰氧化物LaSr2Mn1.9Cu0.1O7多晶.用X射线衍射仪、超导量子干涉仪、直流四探针法对其结构和磁电特性进行了研究.结果表明,样品为Sr3Ti2O7型单相多晶,属四方晶系,空间群为I4/mmm,晶胞参数为a=0.38708nm,c=1.99772nm.此材料呈现出一种典型的自旋玻璃特性,在T=225K发生自旋冻结.Cu的替代破坏了体系的铁磁交换作用,并引入超交换作用.电性测量表明,此材料呈现出颗粒间磁电阻效应且在整个观察的温区样品呈现绝缘体特性,其输运特性属于最近邻小极化子跃迁.
参考文献
| [1] | Jin S;Tiefel T H;MoComack M et al.[J].Science,1994,264:413. |
| [2] | Ramirez A P .[J].Journal of Physics:Condensed Matter,1997,9(39):8171. |
| [3] | Nair S;Banerjee A .[J].Physical Review B,2004,70:104427. |
| [4] | Dho J;Kim W S;Hur N H .[J].Physical Review B,2001,65:24404. |
| [5] | Motitomo Y;Asamitsu A;Kuwahara H et al.[J].Nature,1996,380:141. |
| [6] | Wilkins S B;Spencer P D;Beale T A .[J].Physical Review B,2003,67:205110. |
| [7] | Biswas S;Chatterjee S;Chatterjee P .[J].Physical Review B,2002,66:214403. |
| [8] | Weigand F;Gold S;Schmid J .[J].Applied Physics Letters,2002,81:2035. |
| [9] | Mydosh J A.Spin Glasses:An Experimeatal Introduction[M].London:taylor and Francis,1993 |
| [10] | 陈春霞,章建辉,钱天,周桃飞,李慧玲.锰位Cu离子掺杂对层状锰氧化物La1.2Ca1.8Mn2O7电磁性能的影响[J].材料科学与工程学报,2005(01):23-26. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%