采用高能球磨结合高温渗氮方法制备了Cr18Mn12Mo3N无镍高氮不锈钢粉末,随后利用冷压烧结工艺获得了无镍高氮奥氏体不锈钢材料.结果表明:制备的高氮复合粉末近球形,具有良好的成形性;Cr18Mn12Mo3N不锈钢的最佳烧结温度为1250℃,相对密度达到97.1%,氮含量为0.79%(质量分数);经过1150℃固溶处理水冷后能获得完全奥氏体组织,其钝化电位范围宽,点蚀电位高,抗点蚀性能显著优于316L不锈钢.
参考文献
| [1] | Yamamoto A;Kohyama Y;Kuroda D et al.[J].Materials Science and Engineering C,2004,24(6-8):737. |
| [2] | Uggowitzer P J;Magdowski R;Speidel M O et al.[J].ISIJ International,1996,36(07):901. |
| [3] | Sumita M;Hanawab T;Teoh S H .[J].Materials Science and Engineering C,2004,24(6-8):753. |
| [4] | Simmons J W .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1996,207:159. |
| [5] | 张洪涛,丁春华,郭永峰,杨志懋,丁秉钧.机械合金化PM304粉末的烧结特性[J].稀有金属材料与工程,2007(02):335-338. |
| [6] | Uggowitzer P J;Bahre W F;Speidel M O et al.[J].Advances in Powder Metallurgy and Particulate Materials,1997,18(03):113. |
| [7] | Nakada N;Hirakawa N;Tsuchiyama T et al.[J].Scripta Materialia,2007,57(01):153. |
| [8] | Tandon R;Simmons J W;Covino B S et al.[J].International Journal of Powder Metallurgy,1998,34(08):47. |
| [9] | Speidel M O;Pedrazzoli R M .[J].Materials Performance,1992,31(09):59. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%