引入元素Nb对SO42-/ZrO2进行改进,制备了SO42-促进的Zr-Nb新型二元氧化物固体超强酸催化剂SO42-/ZrO2-Nb2O5.以合成乙酸正丁酯为探针反应,考察了该催化剂的制备工艺,确定了最适宜的制备条件:催化剂中Nb2O5的质量分数为3%,浸渍液硫酸浓度为1.0 mol·L-1,焙烧温度为600 ℃时,酯化率可达到95.3%.采用IR光谱法分析了不同制备条件下催化剂的性能.
参考文献
| [1] | Olah G A;Prakhash G K;Sommer J.Superacids[M].New York:wiley,1985 |
| [2] | 缪长喜;华伟明;陈建民 et al.[J].Science in China(Series B)[中国科学(B辑)],1996,26(03):275. |
| [3] | 李淑敏;郭海福;闫鹏 et al.[J].Petro Chemical Technology(石油化工),2008,37(02):169. |
| [4] | 郭海福;朱正峰;闫鹏 et al.[J].Petro Chemical Technology (石油化工),2007,36(06):565. |
| [5] | Guo Haifu;Yan Peng;Hao Xiangying et al.[J].Materials Chemistry and Physics,2008,112(03):1065. |
| [6] | 陈少峰,郭海福,郝向英,闫鹏.固体超强酸催化剂Ni/SO42--SnO2的制备与表征[J].分子催化,2009(04):339-345. |
| [7] | Husni R Alul;Gilbert J McEwan .[J].J Org hem,1972,37(21):3323. |
| [8] | Dan Fraenkel .Structure of Sulfated Metal Oxides and Its Correlation with Catalytic Activity[J].Industrial & Engineering Chemistry Research,1997(1):52-59. |
| [9] | 蒋平平;卢冠忠 .[J].Modern Chemical Industry (现代化工),2002,22(07):13. |
| [10] | 菅盘铭,徐林,高强,沈常美,孙荣夫.金属掺杂纳米固体超强酸SO2-4/ZrO2的IR考察[J].光谱学与光谱分析,2005(03):356-359. |
| [11] | 崔秀兰;林明丽;李淑英 et al.[J].Chinese Rare Earth s(稀土),2001,22(02):64. |
| [12] | 张强,矫庆泽,闵恩泽.固体超强酸（SO24-/ZrO2）的异丁烷/1-丁烯烷基化反应性能和失活研究[J].高等学校化学学报,2005(06):1130-1132. |
| [13] | 危春玲;陈丰秋;张欢欢 et al.[J].Industrial Catalysis(工业催化),2004(12):46. |
| [14] | 高滋.ZrO2/SO42-超强酸体系形成过程的研究[J].高等学校化学学报,1992(12):1498-1502. |
| [15] | Corma A .[J].Chemical Research,1995,95(03):597. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%