以NH4Al(SO4)2·12H2O、Y2O3、Nd2O3为原料,NH4 HCO3为沉淀剂,采用顺序共沉淀法制备Nd:YAG粉体.并研究了碳酸氢铵浓度对粉体性能的影响,研究结果表明:较佳的碳酸氢铵浓度为1.0 mol/L.制得的粉体颗粒尺寸小,粒度分布窄,分散性好,具有良好的烧结活性,在1800℃真空烧结15 h制备了Nd:YAG透明陶瓷,其近红外波段的透过率为78％.断面和表面形貌显示陶瓷晶粒尺寸均匀,晶界清晰,结晶性好,瓷体致密,平均晶粒尺寸约为15 μm.
参考文献
| [1] | Ji-Guang Li;Takayasu Ikegami;Jong-Heun Lee;Toshiyuki Mori .Low-temperature fabrication of transparent yttrium aluminum garnet (YAG) ceramics without additives[J].Journal of the American Ceramic Society,2000(4):961-963. |
| [2] | A.K.Pradhan;Kai Zhang;G.B.Loutts .Synthesis of neodymium-doped yttrium aluminum garnet (YAG) nanocrystalline powders leading to transparent ceramics[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2004(9):1291-1298. |
| [3] | Sekita M;Haneda H;Yanagitani T et al.Induced emission cross section of Nd:Y3 Al5 O12 ceramics[J].Journal of Applied Physics,1990,67(01):453-458. |
| [4] | Y. Rabinovitch;D. Tetard;M.D. Faucher;M. Pham-Thi .Transparent polycrystalline neodymium doped YAG: synthesis parameters, laser efficiency[J].Optical materials,2003(1/2):345-351. |
| [5] | 闻雷,孙旭东,马伟民.固相反应法制备Nd：YAG透明陶瓷[J].无机材料学报,2004(02):295-301. |
| [6] | Tachiwaki T.;Hirota K.;Ikegami T.;Yamaguchi O.;Yoshinaka M. .Novel synthesis Of Y3Al5O12 (YAG) leading to transparent ceramics[J].Solid State Communications,2001(10/11):603-606. |
| [7] | 张俊计,黄莉萍,徐军.Nd：YAG透明陶瓷的烧成及其显微结构[J].硅酸盐学报,2005(06):678-682. |
| [8] | Naoya Matsushita;Noriyoshi Tsuchiya;Katsuto Nakatsuka;Takakimi Yanagitani .Precipitation and calcination processes for yttrium aluminum garnet precursors synthesized by the urea method[J].Journal of the American Ceramic Society,1999(8):1977-1984. |
| [9] | Ramanathan S;Roy S K;BhatY J .Transparent YAG from powder prepared by homogeneous precipitation reaction-Al (NO3) 3 + Y (NO3) 3 +(NH4)2SO4 + CO(NH2)2[J].Journal of Materials Science Letters,2001,20:2119-2121. |
| [10] | Lu JR.;Prabhu M.;Xu JQ.;Ueda K.;Yagi H.;Yanagitani T. Kudryashov A.;Song J. .High-power Nd : Y3Al5O12 ceramic laser[J].Japanese journal of applied physics,2000(10B):L1048-L1050. |
| [11] | Ji-Guang Li;Takayasu Ikegami .Co-precipitation synthesis and sintering of yttrium aluminum garnet (YAG) powders: the effect of precipitant[J].Journal of the European Ceramic Society,2000(14/15):2395-2405. |
| [12] | Li J-G.;Ikegami T. .Well-sinterable Y_3A1_5O_(12) powder from carbonate precursor[J].Journal of Materials Research,2000(7):1514-1523. |
| [13] | Wang H Z;Gao L;Koichi N .Synthesis of nanoscaled yttrium aluminum garnet powder by the co-precipitation method[J].Materials Science and Engineering,2000,288(01):1-4. |
| [14] | 丁志立,陈嵩,韩杰才.以碳酸氢铵为沉淀剂制备纳米钇铝石榴石粉体[J].材料工程,2005(02):48-50. |
| [15] | Ikesue A;Aung YL .Ceramic laser materials[J].Nature photonics,2008(12):721-727. |
| [16] | 刘文斌,寇华敏,潘裕柏,唐木智明,李江,郭景坤.高透光率Nd：YAG透明陶瓷的制备与性能研究[J].无机材料学报,2008(05):1037-1040. |
| [17] | 四川大学工科基础化学教学中心.近代化学基础[M].北京:高等教育出版社,2002:313-314. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%