以Fe16A12Cr预合金粉末为原料,采用模压成形、真空烧结的方法制备了Fe16A12Cr多孔材料,研究了粉末成形压力与Fe16A12Cr多孔材料性能的关系.结果表明:小于31μm的Fe16A12Cr粉末的压制成形性能较差,压坯强度低；烧结过程中,厚度收缩远大于径向收缩,并随着成形压力的增大而减小；在较高的烧结温度下,成形压力和烧结时间对径向收缩几乎没有影响；而孔隙度、最大孔径和透气度随着成形压力的增大而降低,并随烧结时间延长而增大;增大成形压力,延长烧结时间,有利于提高Fe16A12Cr多孔材料的剪切强度.
参考文献
| [1] | Sundar R S;Sastry D H .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2010,347(1-2):86. |
| [2] | Rosas G;Esparza R;Bedolla-Jacuinde A et al.[J].Journal of Materials Engineering and Performance,2009,18(01):57. |
| [3] | Vedula K;Stepheus J R.Pennsylvania Materials Research Society[M].,1987:381. |
| [4] | Xing Yi;Ma Hongqiu;Kuang Chunjiang .[J].Powder Metallurgy Technology,2005,123(14):263. |
| [5] | Xu Jinghua;Geng Haoran;Sun Jiawei et al.[J].Special Casting & Nonferrous Alloys,2010,30(04):364. |
| [6] | 周芸 .[D].Kunming:Kunming Institute of Technology,2007. |
| [7] | 庞厚君,叶以富,陈斌.多孔Fe3Al金属间化合物的试验研究[J].金属热处理,2006(03):55-58. |
| [8] | Lapin J .[J].Materials Letters,2004,58(24):3007. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%