介绍电沉积硅烷Sol-gel薄膜的原理、方法、用途与研究进展，并着重介绍电沉积硅烷薄膜在金属表面防护处理中的应用。针对防护性的特殊要求，提出电沉积硅烷薄膜研究中的难点与展望。
The principles, methodologies and implications of electrochemically generated silane film materials are reviewed along with some selected recent trends in the fields of functionalized and anti-corrosive sol-gel silica/organosilica films. As a major concern, the recent trends of the electro-assisted generation of organosilica films for corrosion protection are emphasized. The difficulties and the prospective in the study of electrodeposited anti-corrosive silane films are also discussed.
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] | |
| [8] | |
| [9] | |
| [10] | |
| [11] | |
| [12] | |
| [13] | |
| [14] | Subramanian V, Van Ooij W J. Effect of the amine functional group on corrosion rate of iron coated with films of organofunctional silanes [J]. Corrosion, 1998, 54(3): 204-215[2] Subramanian V, Van Ooij W J. Silane based metal pretreatments as alternatives to chromating [J]. Surf. Eng., 1999, 15(2): 168-172[3] Van Ooij W J, Zhu D Q. Electrochemical impedance spectroscopy of bis-[triethoxysilypropyl]tetrasulfide on Al 2024-T3 substrates [J].Corrosion, 2001, 57(5): 413-427[4] Franquet A, Le Pen C, Terryn H. Effect of bath concentration and curing time on the structure of nonfunctional thin organosilane layers on aluminum [J]. Electrochim.Acta, 2003, 48(9): 1245-1255[5] Sundararajan G P, Van Ooij W J. Silane based pretreatments for automotive steels [J]. Surf. Eng., 2000, 16(4): 315-320[6] Zhu D Q, Van Ooij W J. Corrosion protection of AA 2024-T3 by bis-[3-(triethoxysilyl)propyl] tetrasulfide in sodium chloride solution. Part 2: Mechanism for corrosion protection [J]. Corros.Sci., 2003, 45(10): 2177-2197[7] Van Ooij W J, Zhu D Q, Prasad G. Silane based chromate replacements for corrosion control, paint adhesion,and rubber bonding [J]. Surf. Eng., 2000, 16(5): 386-396[8] Hu J M, Liu X L, Zhang J Q. Corrosion protection of Nd-Fe-B magnets by silanization [J]. Prog. Org. Coat., 2006, 55(4): 388-392[9] Zucchi F, Grassi V, Frignani A. Inhibition of copper corrosion by silane coatings [J]. Corros. Sci., 2004, 46(11): 2853-2865[10] Zhu D Q, Van Ooij W J. Enhanced corrosion resistance of AA 2024-T3 and hot-dip galvanized steel using a mixture of bis-[triethoxysilylpropyl] tetrasulfide and bis-[trimethoxysilylpropyl]amine[J]. Electrochim.Acta, 2004, 49(7): 1113-1125[11] Palanivel V, Zhu D Q, Van Ooi W J. Nanoparticle-filled silane films as chromate replacements for aluminum alloys [J]. Prog.Org. Coat., 2003, 47(3-4): 384-392[12] Cabral A M, Trabelsi W, Serra R. The corrosion resistance of hot dip galvanised steel and AA 2024-T3 pre-treated with bis-[triethoxysilylpropyl] tetrasulfide solutions doped with Ce(NO3)3 [J]. Corros. Sci., 2006, 48(11): 3740-3758[13] Song Y K, Mansfeld F. Development of a molybdate-phosphate-silane-silicate (MPSS) coating process for electrogalvanized steel [J].Corros. Sci., 2006, 48(1): 154-164[14] Quinet M, Neveu B, Moutarlier V. Corrosion protection of sol-gel coatings doped with an organic corrosion inhibitor: Chloranil [J]. Prog. Org. Coat., 2007, 58(1): 46-53[15] Liu L, Hu J M, Leng W H. Novel bis-silane/TiO2 bifunctional hybrid films for metal corrosion protection both under ultraviolet irradiation and in the dark [J]. Scr. Mater., 2007, 57: 549-552[16] Liu L, Hu J M, Zhang J Q. Progress in anti-corrosive treatment of metals by silanization [J]. J. Chin. Soc. Corros. Prot., 2006, 26(1): 59-64 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%