通过TG、物相分析、XPS、XRD、SEM-EDS等手段研究铁酸锌选择性还原反应机理，考察铁酸锌质量损失和分解特征、物相转变过程和产物层形貌变化以及Zn 2+与Fe2+的离子迁移行为。结果表明：反应表现为失氧过程，还原产生的Fe2+使铁酸锌分解产生ZnO，ZnO含量与Fe2+含量线性相关。Fe2+向铁酸锌内部迁移替代Zn2+， Zn2+则向外部迁移并富集于表面，促使ZnO在表面形成。铁酸锌逐步向磁铁矿转变，Fe2+的嵌入和锌的迁出使铁酸锌晶胞参数先增大后减小，还原产物为ZnO和含锌的磁铁矿。颗粒产物层中的还原产物相互夹杂，并包裹着未反应的铁酸锌。
The selective reduction mechanism of zinc ferrite was studied by TG, phase analysis, XPS, XRD and SEM-EDS. The mass loss, decomposition features of zinc ferrite, ionic migration behavior of Zn 2+ and Fe2+ ions, phase transformation process and morphological change of product layer were investigated. The results show that reaction is oxygen loss process. The reduced Fe2+ made ZnO separated from zinc ferrite, the content of ZnO has a significant linear correlation with the content of Fe2+. Fe2+ migrates into the inner zinc ferrite to substitute Zn2+, while Zn2+ moves out and enriches on the surface, promoting the formation of ZnO. Zinc ferrite transforms to magnetite, the lattice parameter of zinc ferrite increases and then decreases due to the intercalation of Fe2+ and the emigration of Zn2+. The reduction products are zinc oxide and zinc-containing magnetite. The reduction products coexist with each other in the product layer and unreacted zinc ferrite is covered with the product layer.
参考文献
| [1] | LI Mi, PENG Bing, CHAI Li-yuan, PENG Ning, YAN Huan, HOU Dong-ke. Recovery of iron from zinc leaching residue by selective reduction roasting with carbon[J]. Journal of Hazardous Materials, 2012, 238(10):323-330.,2012. |
| [2] | 王纪明,彭兵,柴立元,李密,彭宁.锌浸渣还原焙烧-磁选回收铁[J].中国有色金属学报（英文版）,2012(05):1455-1461. |
| [3] | 韩俊伟,刘维,覃文庆,柴立元,郑永兴,杨康.高铁锌焙砂选择性还原焙烧-两段浸出锌[J].中国有色金属学报,2014(02):511-518. |
| [4] | RAGHAVAN V. Fe-O-Zn(iron-oxygen-zinc)[J]. Journal of Phase Equilibria and Diffusion, 2010, 31(4):373-376.,2010. |
| [5] | 梁美生 .铁酸锌高温煤气脱硫行为及气氛效应研究[D].太原理工大学,2005. |
| [6] | GHEISARI M, MOZAFFARI M, ACET M, AMIGHIAN J. Preparation and investigation of magnetic properties of wüstite nanoparticles[J]. Journal of Magnetism and Magnetic Materials, 2008, 320(21):2618-2621.,2008. |
| [7] | 李密 .锌焙砂选择性还原与铁锌分离的基础研究[D].中南大学,2013. |
| [8] | O'NEILL H S C, NAVROTSKY A. Simple spinels; crystallographic parameters, cation radii, lattice energies, and cationdistribution[J]. American Mineralogist, 1983, 68(1/2):181-194.,1983. |
| [9] | 傅毛生,陈林深,李建国,陈诵英.还原条件对NiFe2O4-δ结构稳定性及其催化分解CO2活性的影响[J].燃料化学学报,2007(04):431-435. |
| [10] | 张春雷,吴通好,杨洪茂,姜玉子,彭少逸.氧缺位的磁铁矿型化合物转化CO2成C的研究[J].无机化学学报,1996(01):61-66. |
| [11] | 朴玲钰,李春虎,李彦旭.ZnFe2O4高温煤气脱硫剂的还原与硫化[J].高校化学工程学报,2001(06):546-551. |
| [12] | KODAMA T, TABATA M, SANO T, TSUJI M, TAMAURA Y. XRD and Mössbauer studies on oxygen-deficient Ni(Ⅱ)-bearing ferrite with a high reactivity for CO 2 decomposition to carbon[J]. Journal of Solid State Chemistry, 1995, 120(1):64-69.,1995. |
| [13] | MAKOVEC D, DROFENIK M. Non-stoichiometric zinc-ferrite spinel nanoparticles[J]. Journal of Nanoparticle Research, 2008, 10(1):131-141.,2008. |
| [14] | TONG L F. Reduction mechanisms and behaviour of zinc ferrite-Part 1:Pure ZnFe2O4 [J]. Mineral Processing and Extractive Metallurgy, 2001, 110(1):14-24.,2001. |
| [15] | BERA S, PRINCE A A M, VELMURUGAN S, RAGHAVAN P S, GOPALAN R, PANNEERSELVAM G, NARASIMHAN S V. Formation of zinc ferrite by solid-state reaction and its characterization by XRD and XPS[J]. Journal of materials science, 2001, 36(22):5379-5384.,2001. |
| [16] | DRUSKA P, STEINIKE U, ŠEPELÁK V. Surface structure of mechanically activated and of mechanosynthesized zinc ferrite[J]. Journal of Solid State Chemistry, 1999, 146(1):13-21.,1999. |
| [17] | ŠEPELÁK V, STEINIKE U, UECKER D C, WIßMANN S, BECKER K D. Structural disorder in mechanosynthesized zinc ferrite[J]. Journal of Solid State Chemistry, 1998, 135(1):52-58.,1998. |
| [18] | 张燕娟,黎铉海,潘柳萍,韦岩松.机械活化对铟铁酸锌溶解动力学及物化性质的影响[J].中国有色金属学报,2012(01):315-323. |
| [19] | 张惠斌.矿石和工业产品化学物相分析[M].北京:冶金工业出版社, 1992:138-352. ZHANG Hui-bin. Chemical phase analysis of ores and industrial products[M]. Beijing:Metellurgical Industry Press, 1992:138-352.,1992. |
| [20] | 夏秀文,何维,黄津梨,梁建烈.最小二乘法精确测定Gd3Co1-xVx的点阵常数和固溶度[J].稀土,2009(01):22-25. |
| [21] | 梁敬魁. 粉末衍射法测定晶体结构[M]. 北京:科学出版社, 2003:340-342, 540-542. LIANG Jing-kui. Crystal structure determination by X-ray powder diffraction[M]. Beijing:Science Press, 2003:340-342, 540-542.,2003. |
| [22] | MILLS P, SULLIVAN J L. A study of the core level electrons in iron and its three oxides by means of X-ray photoelectron spectroscopy[J]. Journal of Physics D:Applied Physics, 1983, 16(5):723.,1983. |
| [23] | YAMASHITA T, HAYES P. Analysis of XPS spectra of Fe2+ and Fe3+ ions in oxide materials[J]. Applied Surface Science, 2008, 254(8):2441-2449.,2008. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%