研究了施加稳恒磁场(H=0～0.7 T)对电沉积铁-镍合金箔的影响.测定了垂直电流方向,不同强度磁场下的电流效率、合金组成及合金箔的磁性能,并用扫描电镜和X射线衍射观察合金箔的微观形貌和结构,分析讨论了稳恒磁场对这些性能的影响规律.结果表明;与不施加磁场相比,施加垂直磁场后合金箔表面更均匀、细致、平整;合金箔铁含量提高约14%;合金箔(111)晶面取向程度增强,磁性能有所改善;但铁-镍合金电镀的电流效率呈先增加后下降的趋势.
参考文献
| [1] | 李廷举,温斌,张志峰,金俊泽.电磁场作用下材料加工新技术[J].大连理工大学学报,2000(Z1):61-64. |
| [2] | Asai S G;Sassa K S;Tahashi M.Crystal Orientation of Non Magnetic Materials by Imposition of a High Magnetic Field[J].Science and Technology of Advanced Materials,2003(04):455. |
| [3] | Devos O;Olivier A;Aaboubi O et al.Magnetic Field on Nickel Electrodeposition[J].Eiectrochem Soc,1998,145(02):401. |
| [4] | Krause A;Uhlemann M;Gebert A et al.The Effect of Mag-netic Fields on the Electrodeposition of Cobalt[J].Electrochimica Acta,2004,49:4127. |
| [5] | Yoshihumi Ootake;Kensuke Sassa;Takashi Yamada;Shigeo Asai .Control of compositions electrodeposited in a Ni-Zn system by imposition of a high magnetic field[J].日本金属学会誌,2003(1):1-6. |
| [6] | 牟世辉,袁艳,姚淑霞.稳恒磁场对电镀铬的影响[J].沈阳工业学院学报,2004(02):83-85. |
| [7] | 温艳玲,钟云波,任忠鸣,邓康,徐匡迪.平行强磁场对电沉积镍-铁合金膜显微组织的影响（一）匀强磁场实验研究部分[J].电镀与精饰,2006(04):1-4. |
| [8] | 高鹏,杨中东,薛向欣,樊占国.磁场影响下的电沉积[J].材料保护,2006(08):38-42. |
| [9] | 杨中东,高鹏,薛向欣,樊占国,刘素兰,国栋.稳恒磁场下Ni-W合金镀膜的制备与耐蚀性[J].中国有色金属学报,2006(10):1710-1715. |
| [10] | Daheum Kim;D. -Y. Park;B. Y. Yoo;P. T. A. Sumodjo;N. V. Myung .Magnetic properties of nanocrystalline iron group thin film alloys electrodeposited from sulfate and chloride baths[J].Electrochimica Acta,2003(7):819-830. |
| [11] | Fshar A;Dolati A G;Ghorbani M .Electrochemical Charac-terization of the Fe-Ni Alloy Electrodeposition from Chloride-Citrate Glycolic Acid Solutions[J].Materials Chemistry and Physics,2002,77:352. |
| [12] | Kieling VC .Parameters influencing the electrodeposition of Ni-Fe alloys[J].Surface & Coatings Technology,1997(2/3):135-139. |
| [13] | 杨余芳,龚竹青,罗北平,马玉天,阳征会.电沉积Fe-Ni合金箔的工艺和性能研究[J].电镀与精饰,2006(01):5-9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%