采用脉冲氩弧焊接工艺、高温加速模拟、高温持久实验研究了不同焊缝蠕变强度匹配条件下马氏体耐热钢9Cr1MoVNbN与贝氏体耐热钢12Cr2MoWVTiB异种钢焊接接头的高温强度、界面蠕变损伤及破坏特征. 研究结果表明, 焊前523 K预热、焊后1023 K x 1 h回火条件下, 接头的力学性能优异. 加速模拟运行500, 1000和1500 h后低匹配焊接接头的界面蠕变损伤最严重, 发生了界面蠕变断裂, 早期失效倾向较大; 中匹配接头的蠕变损伤最小, 仅发现个别孤立蠕变孔洞,早期失效倾向最小, 中匹配接头在923 K下的持久强度(105)与低匹配接头比较接近; 高匹配接头在923 K下的持久强度(105)最低, 蠕变孔洞几乎连成裂纹, 蠕变损伤和早期失效较大.因此, 对于上述异种钢焊接接头采用中匹配焊缝较为合理.
Abstract The creep rupture strength, creep damage and characteristics of interfacial failure of dissimilar welded joint between martensite (9Cr1MoVNbN) and bainite steel(12Cr2MoWVTiB) are been investigated by means of argon gas shielded tungsten pulsed arc welding, high temperature accelerated simulation, creep rupture test, in view of dissimilar welded joint between martensite (9Cr1MoVNbN) and bainite steel(12Cr2MoWVTiB).The research results indicate that the interfacial creep damage of undermatching welded joint is very serious, and the interfacial failure occurred, the early failure tendencies are higher than those of overmatching and medium welded joint. The creep damage and early failure tendency of medium matched joint are lower than those of overmatching and undermatching welded joint, and only isolated holes are found in the test. The creep rupture strength ( ) of medium matching joint is almost the same as that of undermatching joint. The creep rupture strength overmatching joint is the least one, therefore, it is reasonable that the medium matched is used for the dissimilar welded joint between martensite and bainite steel. KEY WORDS Martensite heat-resistant steel, bainite heat-resistant steel, dissimilar metal welding joint, creep damage, early failure
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] | |
| [8] | |
| [9] | |
| [10] | |
| [11] | |
| [12] | |
| [13] | |
| [14] |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%