研究了热轧卷取温度对CSP(compact strip production)冷轧深冲板的性能、组织和织构的影响.CSP热轧板组织主要为多边形铁素体,随卷取温度降低,晶粒尺寸略有减小.660℃和680℃卷取的成品冷轧板组织为等轴晶粒,卷取温度不超过600℃时则以"饼型"晶粒为主.力学性能测试表明,低于600℃卷取的成品板屈服强度和抗拉强度较低,其加权平均塑性应变比(rm)可达到1.80以上,伸长率超过49%.随卷取温度升高,成品板的{001}<110>和{110}<110>织构的取向分布密度逐渐升高,{111}织构取向分布密度先升高后降低,{111}<110>和{111}<112>织构取向分布密度差值也是先升后降.

Influence of coiling temperature(CT)on microstructure of hot-rolled low carbon sheet produced by CSP(compact strip production)process,and microstructure and mechanical properties and textures of DQ(Drawing Quality)level cold rolled deep-drawing steel sheet fabricated using the CSP hot rolled sheet were investigated.Microstructure of hot-rolled sheet is composed of polygonal ferrite.As CT decreases,size of ferrite decreases slightly.Microstructure of the cold-rolled sheet produced with CT of 660 ℃ and 680 ℃ is composed of equiaxed grains,and that produced with CT below 600 ℃ exhibits mainly "pie shape" grains.The mechanical property test indicates that the cold rolled sheet prepared with CT below 600 ℃ presents lower yield strength and tension strength,its rm is above 1.80,and the elongation is higher than 49%.As the CT increases,{001}<110> and {110}<110> texture of the cold-rooled sheet is getting stronger,and the difference of orientation distribution density of {111}<110> and {111}<112> texture increases first and then decreases.

参考文献

[1] 殷瑞钰.中国薄板坯连铸连轧的进展[J].钢铁,2008(03):1-9.
[2] 孔学云,王宝峰,金自力,任慧平,张晓燕.冷轧板再结晶退火中组织和织构演变的研究[J].材料热处理学报,2007(04):97-101.
[3] 武磊,刘雅政,刘兴全,洪继要.退火工艺对CSP供冷轧原料的SPCC板性能和织构的影响[J].材料热处理学报,2007(z1):130-133.
[4] 刘正东,程杰锋,董瀚,干勇.热轧带钢卷带及其冷却过程AlN沉淀析出模拟研究[J].钢铁,2004(03):38-42.
[5] 常军,张开华,程兴德,王丹.终轧温度和卷取温度对低碳铝镇静钢性能的影响[J].钢铁钒钛,1999(01):32.
[6] 李新城,陈伟,陈光,张开华.热轧温度控制对冷轧超深冲板深冲性能的影响[J].农业机械学报,2007(06):173-177.
[7] 徐匡迪,刘清友.薄板坯流程连铸连轧过程中的细晶化现象分析[J].钢铁,2005(12):1-9.
[8] 刘清友,梁小恺,王雪莲,李德刚,董瀚.薄板坯连铸连轧流程低碳Al镇静钢组织细化原因探讨[J].钢铁,2005(08):65-69.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%