在母体聚合物中引入的作为造孔剂的聚合物在碳化期间完全分解,从而在碳基体中留下大量的孔隙.通过添加不同种类的聚合物,可以控制活性炭材料的孔径分布.综述了利用这种方法对活性炭材料的孔径分布进行控制的原理和方法,并介绍了这方面的研究进展.
参考文献
| [1] | Sing K S W et al.[J].Pure and Applied Chemistry,1985,57(04):603. |
| [2] | 田中荣治 .[J].エレクトロニク セラミクス,1992,23(11):41. |
| [3] | 松村雄次 .[J].化学と工业,1990,43(03):102. |
| [4] | 乔文明 .超级活性炭的制备及其结构与性能研究[D].中国科学院山西煤炭化学研究所,1993. |
| [5] | Graoly T M O;Wennerberg A N .[J].American Chemical Society,1984,29(02):410. |
| [6] | Oya A.;Alcanizmonge J.;Linaressolano A.;Yoshida S. .FORMATION OF MESOPORES IN PHENOLIC RESIN-DERIVED CARBON FIBER BY CATALYTIC ACTIVATION USING COBALT[J].Carbon: An International Journal Sponsored by the American Carbon Society,1995(8):1085-1090. |
| [7] | Oya A.;Alcanizmonge J.;Linaressolano A.;Yoshida S. .PREPARATION AND PROPERTIES OF AN ANTIBACTERIAL ACTIVATED CARBON FIBER CONTAINING MESOPORES[J].Carbon: An International Journal Sponsored by the American Carbon Society,1996(1):53-57. |
| [8] | Tamai H;Kakii T;Hirota Y et al.[J].Chemistry of Materials,1996,8(01):54. |
| [9] | 安田源;玉井久司 .[J].化学と工业,1992,43(07):536. |
| [10] | Miyanaga S;Yasuda H;Hiwara A et al.[J].Journal of Macromolecular Science:Chemistry,1990,A27(9-11):1344. |
| [11] | Marsh H;Diez M A;Kao K;J Lahayed,P Ehrburgor.Fundamental issues in control of carbon gasification reactivity[M].Kluwer Academic Publishers:Dordrecht,1991:205. |
| [12] | Redriguez Reinoso F;Almela-Alarcon M;Linares-Solano A.Extended Absracts.17th Conference on carbon[C].,1985:273. |
| [13] | Ozaki J;Endo N;Ohizumi W et al.[J].CARBON,1997,35(08):1031. |
| [14] | 远藤伸将;中原雅则;大谷朝男.[A].,1995:232. |
| [15] | Yiannis A;Richard C .[J].Flagan Carbon,1989,27(02):265. |
| [16] | Hatori H;Yasuda Y;Shiraishi M .[J].Carbon,1992,30(02):303. |
| [17] | Hatori H;Yasuda Y;Shiraishi M .[J].Carbon,1992,30(05):763. |
| [18] | Hatori H;Yasuda Y;Shiraishi M.Proceedings of international conference on carbon ,CARBON' 96[C].ExtendedAbstr Newcastle,upon tyne:416. |
| [19] | 吴培熙;张留成.聚合物共混改性原理及工艺[M].北京:中国轻工业出版社,1982:124. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%