采用分阶振幅和恒定振幅对不同薄金属材料(0.1 mm厚的铝片和镀镍钢片搭接成锂电池极耳)进行超声焊接,利用3D共聚焦显微镜分析了焊接接头表面形貌特征,并通过剥离试验测其接头强度.结果表明:与恒定振幅相比,采用分阶振幅超声焊接铝片和镀镍钢片可获得更高的接头强度,且标准差稳定,减少接头表面与工具头的粘附,剥离试验后接头表面相对平整,减少了焊接过程中较软金属中产生的裂纹.
参考文献
| [1] | HETRICK B E T;BAER J R;ZHU W et al.Ultrasonic metal welding process robustness in aluminum automotive body construction applications[J].Welding Journal,2009,88(09):149-158. |
| [2] | 李东 .层叠式锂电池制造中金属极片的超声波焊接工艺优化方法[D].上海交通大学,2013. |
| [3] | TSUJINO J;SUGIMOTO E.Welding characteristics of aluminum,copper,nickel and aluminum alloy with alumina coating using ultrasonic complex vibration welding equipments[A].,2009:1211-1214. |
| [4] | AL-SARRAF Z;LUCAS M .A study of weld quality in ultrasonic spot welding of similar and dissimilar metals[J].Journal of Physics:Conference Series,2012,382:012013(17. |
| [5] | GUTENSOHN M;WAGNER G;EIFLER D .Reduction of the adherence of aluminum on ultrasonic welding tools[J].Dvs Berichte,2005,237:452-459. |
| [6] | 邢丽;朱蕾;杨剑赟 等.焊接参数对TC4钛合金线性摩擦焊焊缝成形的影响[J].机械工程材料,2014,38(07):43-49. |
| [7] | T. H. Kim;J. Yum;S. J. Hu;J. P. Spicer;J. A. Abell .Process robustness of single lap ultrasonic welding of thin, dissimilar materials[J].CIRP Annals,2011(1):17-20. |
| [8] | M. BABOI;D. GREWELL .Evaluation of Amplitude Stepping in Ultrasonic Welding[J].Welding Journal,2010(8):161-s-165-s. |
| [9] | 曹凤国.超声加工技术[M].北京:化学工业出版社,2005 |
| [10] | 李国栋,栗卓新,张天理,马司鸣.超声波辅助钎焊技术的研究进展[J].机械工程材料,2013(01):1-4. |
| [11] | 李亚江;王娟.特种焊接技术及应用[M].北京:化学工业出版社,2004 |
| [12] | 杨圣文,汤勇.铜片-铜管的超声波焊接机理研究[J].焊管,2005(05):28-31. |
| [13] | PARK D S;KIM J H;SEO J S .Ultrasonic welding of Ni thin sheet[J].IJMMME,2013,1(02):133-137. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%