采用高温热蒸镀方法处理在金刚石表面镀覆上了SiO2/SiC晶粒复合涂层,同时研究了热处理温度和Al助剂对金刚石表面形成SiO2/SiC晶粒复合涂层的影响.研究结果表明,在较低温度(1400℃),金刚石表面形成许多SiC和SiO2和SiC颗粒.当温度升高到1450℃时,金刚石表面镀覆了良好的SiO2/SiC复合涂层,形成了许多SiO2和SiC颗粒、微米棒与晶须.Si粉中添加适量的Al(5 mass%)就会促进Si的蒸发,在1400℃时金刚石表面就会形成大量的SiO2和SiC颗粒、微米棒与晶须.

参考文献

[1] A.G.Mamalis;M.Horvath.Diamond grinding of super-hard materials[J].Journal of Materials Processing Technology,20001/3(1/3):120-125.
[2] Heung-Kil Park;Hiromichi Onikura;Osamu Ohnishi;Ahmad Sharifuddin.Development of micro-diamond tools through electroless composite plating and investigation into micro-machining characteristics[J].Precision Engineering,20103(3):376-386.
[3] B. Felde;A. Mehner;S. Kohlscheen.Deposition of alumina coatings on monocrystalline diamonds by sol-gel techniques[J].Diamond and Related Materials,20013-7(3-7):515-518.
[4] Weida Hu;Long Wan;Xiaopan Liu;Qiang Li;Zhiqi Wang.Effect of TiO_2/Al_2O_3 film coated diamond abrasive particles by sol-gel technique[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,201113(13):5777-5783.
[5] N. Yan;D.P. Zhao;L Wang.Preparation and sintering of silica-coated ultrafine diamonds-vitrified bond composite powders[J].International Journal of Refractory Metals & Hard Materials,2014Mar.(Mar.):212-215.
[6] 王猛;李成明;陈良贤;刘金龙;郭建超;魏俊俊;黑立富;吕反修.金刚石自支撑膜衬底生长立方Y2O3薄膜的性能[J].材料热处理学报,2014(7):177-181.
[7] Zhu, G;Zou, XP;Cheng, J;Wang, MF;Su, Y.Synthesis of straight Y-shaped SiOx nanorods by a simple thermal evaporation method[J].Solid State Communications,20085/6(5/6):243-246.
[8] Kai Chen;Zhaohui Huang;Juntong Huang.Synthesis of SiC nanowires by thermal evaporation method without catalyst assistant[J].CERAMICS INTERNATIONAL,20132(2):1957-1962.
[9] Chhikara, Deepak;Kumar, M. Senthil;Srivatsa, K. M. K..On the synthesis of Zn/ZnO core-shell solid microspheres on quartz substrate by thermal evaporation technique[J].Superlattices and microstructures,2015:368-377.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%