采用两种含有羧基官能团的共聚物作为增容剂,通过反应挤出法制备了尼龙6/乙烯-醋酸乙烯酯共聚物(EVA)共混合金;并对合金的力学性能和亚微形态进行了研究.结果表明,通过挤出过程中增容剂的羧基官能团与尼龙6反应,可提高尼龙6与EVA的界面粘结性,从而使合金获得较高的缺口冲击强度,同时合金的断裂伸长率也显著提高SEM研究显示,EVA与尼龙6的相容性较差,基体中EVA粒子直径约为1.5——2.0μm;而添加增容剂后,可以提高EVA在基体中的分散性,并使分散相粒子的直径显著减小
Blends of Nylon 6 matrix (800mg/g) and ethylene-vinyl acetate copolymer (EVA) impact modifier (200mg/g) were prepared by reactive extrusion with compatibilizers with fuctional carboxyl group,included one of ethylene-acrylic acid copolymer (Nucrel) and eth