采用低温直流-脉冲阳极氧化技术对多孔NiTi合金表面进行改性,分析直流-脉冲阳极氧化过程,利用XPS、SEM、动电位极化对阳极氧化膜的组成、形貌以及耐腐蚀性进行研究,观察阳极氧化前后多孔NiTi合金在模拟人工体液中Ni离子释放行为.研究结果表明在直流3 A、脉冲6 A下阳极氧化的多孔NiTi合金表面形成了一层均匀的多孔氧化膜,其厚度在190 nm左右,主要成分为Ti的氧化物,阳极氧化后多孔NiTi合金的耐腐蚀性显著提高,其Ni离子释放速率大幅度降低.
参考文献
| [1] | Zhao Y;Taya M;Kang Y S et al.[J].ACTA MATERIALIA,2005,53(02):337. |
| [2] | Otsuka K;Ren X B .[J].INTERMETALLICS,1999,7(05):511. |
| [3] | Barrett R D;Bishara S E;Quinn J K .[J].American Journal of Orthodontics and Dentofacial Orthopedics,1993,103(01):8. |
| [4] | Dunlap C L;Vincent S K;Barker B F .[J].Journal of the American Dental Association,1989,118(04):449. |
| [5] | Firstov G;Vitchev R;Kumar H;Blanpain B;Van Humbeeck J .Surface oxidation of NiTi shape memory alloy.[J].Biomaterials,2002(24):4863-0. |
| [6] | Green S M;Grant D M;Wood J V .[J].Materials Science&Engineering A,1997,224(1-2):21. |
| [7] | Fili P;Lausmaa J;Musialek J;Mazanec K .Structure and surface of TiNi human implants.[J].Biomaterials,2001(15):2131-2138. |
| [8] | Villermaux F;Tabrizian M;Yahia L H et al.[J].Applied Surface Science,1997,109(01):62. |
| [9] | Lausmaa J;Kasemo B;Mattsson H et al.[J].Applied Surface Science,1990,45:189. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%