采用光学显微镜、扫描电子显微镜研究了HP2-13Cr油管钢在模拟高温高压气井环境中(酸化→返排残酸→采出水)点蚀行为的发展变化.结果表明:HP2-13Cr在服役过程中的点蚀主要在返排残酸阶段产生,残酸是引起HP2-13Cr点蚀的主要原因；统计了不同阶段点蚀坑深度的发展,得到返排残酸期间点蚀速率为7.56 mm/a,采出水期间点蚀发展速率为0.47 mm/a.点蚀坑深度的统计规律符合Gumbel分布,点蚀坑呈浅碟型.
参考文献
| [1] | Cao C N.Nature Environment Corrosion of Materials in China[M].Beijing:Chemical Industry Press,Beijing,2005 |
| [2] | 张毅,李鹤林,陈诚德.我国油井管现状及存在问题[J].焊管,1999,22(5):1 |
| [3] | 徐进,罗平亚,刘映金.高温高压高产腐蚀气井完井管柱及井口装置损坏机理研究[D].四川:西南石油学院,2005 |
| [4] | Zhang G A,Cheng Y F.Electrochemical characterization and computational fluid dynamics simulation of flow-accelerated corrosion of X65 steel in a CO2-saturated oilfield formation water[J].Corros.Sci.,2009,51:87 |
| [5] | He W,Knudsen O (O),Diplas S.Corrosion of stainless steel 316L in simulated formation water environment with CO2-H2S-Cl[J].Corros.Sci.,2009,51:2811 |
| [6] | 李鹤林,白真权,李鹏亮等.模拟CO/H2S环境中APIN80钢的腐蚀影响因素研究[A].第二届石油石化工业用材研究会论文集[C].成都,2001:101 |
| [7] | Marchebois H,Leyer J,SSC performance of a super 13％Cr martensitic stainless steel for OCTG[J].NACE Corros.,2007:07090 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%