以二噻吩(BT)和三联噻吩(TT)为单体,FeCl3为氧化剂,在不同n(FeCl3)/n(单体)比例下,通过固相反应法合成出了聚(二噻吩)(poly(BT))和聚(三噻吩)(poly(TT)).并以傅立叶变换红外光谱、紫外可见吸收光谱、X射线衍射、热重分析和透射电镜等测试方法对聚合物进行了表征,研究了不同n(FeCl3)/n(单体)比例对聚合物结构与性能的影响.结果表明,n(FeCl3)/n(BT)为4:1和n(FeCl3)/n(TT)为8:1时,所得聚合物相对于其它比例下的聚合物表现出了较高的分子量、共轭程度和热稳定.其中,poly(TT)的分子量、共轭程度、热稳定、结晶性等特性随单体与FeCl3比例发生明显变化,但在微观形貌上无明显变化,而poly(BT)则随单体与FeCl3比例变化结果与poly(TT)相反,只是在微观形貌上产生了一定的差异.
参考文献
| [1] | Hoffmann K. J.;Bakken E. .Synthesis and polymerization of 3, 3'-dialkyl-2,2'-bithiophenes[J].Synthetic Metals,2000(1/2):39-44. |
| [2] | Hu X.;Xu LG. .Structure and properties of 3-alkoxy substituted polythiophene synthesized at low temperature[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(26):9147-9154. |
| [3] | Casalbore-Miceli G.;Beggiato G.;Fichera M.;Gallazzi MC.;Camaioni N. .Influence of the supporting electrolyte and of film thickness on the ratio between the crystal and amorphous structure in electrosynthesised poly(4,4 '-dipentoxy-2,2 '-bithiophene)[J].Synthetic Metals,1998(2):143-146. |
| [4] | Wang, JX;Wang, JS;Zhang, XY;Wang, Z .Assembly of polyaniline nanostructures[J].Macromolecular rapid communications,2007(1):84-87. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%