采用Thermecmastor-Z型热模拟机对Haynes230合金进行变形温度为950~1250℃,应变速率为0.001~10 s1范围内的高温压缩试验,并利用OM和TEM分析研究了热变形组织演化特征和动态再结晶形核机制.结果表明:动态再结晶晶粒尺寸和体积分数随着变形温度的升高而增大和增多,随着应变速率的升高而变小和减少;晶界弓出是合金动态再结晶的主要形核机制,项链组织在热变形组织演化过程中起着重要作用;动态再结晶稳态晶粒尺寸Dss与Z参数之间符合幂函数关系.
参考文献
[1] | Sellars C M;McTegart W J .[J].Acta Metallurgica,1966,14:1136. |
[2] | Ueki M;Horie S;Nakamura T .[J].Materials Science and Technology,1987,3:329. |
[3] | Sakai T .[J].Journal of Materials Processing Technology,1995,53:349. |
[4] | Pong D;Gottstein G .[J].Acta Materialia,1997,46(01):69. |
[5] | Belyakov A.;Sakai T.;Miura H. .Dynamic recrystallization under warm deformation of a 304 type austenitic stainless steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):139-147. |
[6] | Brunger E;Wang X;Gottstein G .[J].Scripta Materialia,1998,38(12):1843. |
[7] | Jafari, M;Najafizadeh, A .Correlation between Zener-Hollomon parameter and necklace DRX during hot deformation of 316 stainless steel[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2009(1/2):16-25. |
[8] | Sakai T;Jonas J J .[J].Acta Metallurgica,1984,32:189. |
[9] | MeQueen H J;Ryan N D .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2002,322:43. |
[10] | Prasad Y V R K;Sasidhara S.Hot Working Guide.:A Compendium of Processing Maps[M].Materials Park,OH:ASM International,The Materials Information Society,1997:1. |
[11] | Lu YL;Liaw PK;Wang GY;Benson ML;Thompson SA;Blust JW;Browning PF;Bhattacharya AK;Aurrecoechea JM;Klarstrom DL .Fracture modes of HAYNES (R) 230 (R) alloy during fatigue-crack-growth at room and elevated temperatures[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):122-131. |
[12] | Liu Yi;Hu Rui;Li Jinshan et al.[J].Materials Science and Engineering A,2008,497:238. |
[13] | Liu Yi;Hu Rui;Li Jinshan et al.[J].Journal of Materials Processing Technology,2009,209:4020. |
[14] | 张青 .[D].Hefei:Hefei University of Technology,2008. |
[15] | Somani MC.;Prasad YVRK.;Singh V.;Muraleedharan K. .Mechanical processing and microstructural control in hot working of hot isostatically pressed P/M IN-100 superalloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1):88-99. |
[16] | Monajati H;Jahazi M;Yue S et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2005,36:895. |
[17] | Medeiros S C;Prasad Y V R K;Frazier W G et al.[J].Materials Science and Engineering A,2000,293:198. |
[18] | Guimaraes A A;Jonas J J .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1981,12:1655. |
[19] | 张北江,赵光普,焦兰英,胥国华,秦鹤勇,冯涤.热加工工艺对GH4586合金微观组织的影响[J].金属学报,2005(04):351-356. |
[20] | 康福伟 .[D].哈尔滨:哈尔滨工业大学,2007. |
[21] | Gorelik S S;仝健民.金属与合金的再结晶[M].北京:机械工业出版社,1985:207. |
[22] | McQueen H J;Jonas J J.Plastic Deformation of Materials[M].New York:Academic Press,Inc,1975:393. |
[23] | Sah J P;Richardson G J;Sellars C M .[J].Metal Science Journal,1974,8:325. |
[24] | Roberts W;Boden H;Ahblom B .[J].Metal Science Journal,1979,13:195. |
[25] | Shen G;Semiatin S L;Shivpuri R .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1995,26:1795. |
[26] | Medina S F;Hernandez C A .[J].Acta Materialia,1996,44:165. |
[27] | Bocher P .Thesis for Doctorate[D].Montreal:McgGill University,1998. |
[28] | Semiatin S L;Weaver D S;Fagin P N et al.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2004,35:679. |
[29] | Na Y S;Yeom J T;Park N K et al.[J].Journal of Materials Processing Technology,2003,141:337. |
[30] | Fernández A I;Uranga P;L6pez B et al.[J].Materials Science and Engineering A,2003,361:367. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%