用异丙醇部分取代γ-甲基丙烯酰氧基丙基三甲氧基硅烷（KH-570）的甲氧基,引入空间位阻较大的异丙氧基,使改性后的KH-570水解速率变慢。再用改性KH-570、八甲基环四硅氧烷（D4）与丙烯酸酯类单体乳液聚合,研究有机硅含量对聚合过程和乳胶膜透明性、力学性能等的影响。结果表明,引入异丙氧基后,有机硅耐水解性提高,反应结束仅少量凝胶,固含量在30%左右,转化率保持在80%以上;有机硅含量为21%时,乳液近似为牛顿流体,涂膜综合性能最好,吸水率最低为10%,断裂强度超过1MPa,断裂伸长率达475%。
Isopropyl alcohol was used to modify KH-570,isopropoxy with larger steric hindrance was partially or fully introduced to it,this made the modified production have hydrolysis resistance.The silicone-acrylate emulsions of different silicone content were prepared using vinyl siloxanes and grafting siloxanes.The effects of silicone content on the process of emulsion polymerization and transparence,the mechanical properties of latex film were studied.The results show that the hydrolysis resistance of organsilicone is improved with the introduction of isopropoxy,little coagulation is left in the system;the latex film has excellent general performance when the silicone content reaches 21% of total monomers.
参考文献
| [1] | Hamid Javaherian Naghash;Akram Karimzadeh;Ahmad Reza Massah .Synthesis and Properties of Styrene–Butylacrylate Emulsion Copolymers Modified by Silane Compounds[J].Journal of Applied Polymer Science,2009(2):1037-1044. |
| [2] | Hamid Javaherian Naghash;Ahmad Reza Momeni;Hamid Allan;Ahmad Reza Massah;Shahla Ataie .Preparation and properties of silicone-containing poly(methyl methacrylate) gels[J].Polymer international,2005(11):1564-1571. |
| [3] | Ming J. Chen;Fred D. Osterholtz;Eric R. Pohl;Philbert E. Ramdatt;Antonio Chaves;Valerie Bennett .Silanes in High Solids and Water- borne Coatings[J].JCT,1997(870):43-51. |
| [4] | CHENG YOU KAN;XIANG ZHENG KONG;QING YUAN;DE SHAN LIU .Morphlogical Prediction and Its Application to the Synthesis of Polyacrylate/Polysiloxane Core/Shell Latex Particles[J].Journal of Applied Polymer Science,2001(12):2251-2258. |
| [5] | 欧阳新平,谭春枚,邱学青,杨东杰,邓永红.水溶性苯乙烯-苯乙烯磺酸钠共聚物的合成及分散稳定性能研究[J].高校化学工程学报,2010(04):681-687. |
| [6] | 罗英武,许华君,李宝芳.细乳液聚合制备有机硅/丙烯酸酯乳液及其性能[J].化工学报,2006(12):2981-2986. |
| [7] | 黄世强,彭慧,李盛彪,孙争光.PHMS/BA复合乳液的研究--PHMS对乳液性能的影响及聚合反应机理[J].高分子材料科学与工程,2000(05):22-25. |
| [8] | 徐彦,邢朋,谢洪德,徐国华.聚硅氧烷与丙烯酸酯弹性体的制备及性能[J].高分子材料科学与工程,2009(02):4-7. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%