研究了一种制备Mn3O4的方法,以廉价的硫酸锰为原料,通过控制反应条件制得了高纯度的纳米级Mn3O4.实验结果表明,反应的最佳条件为:加适量乙醇作为分散剂;控制氨水滴加速度使反应时间在2h以上;前驱物在200℃煅烧2h.采用X射线衍射(XRD)、透射电子显微镜(TEM)等手段对产物进行了表征,产物纯度为100%,粒径约为20nm.
A method of preparing Mn3O4 is studied.Using cheap MnSO4 as material,nano-Mn3O4 is gained with high purity through controlling the reaction conditions.The result shows that the optimal condition is as follows:ethanol is added as dispersant; more than 2h is required by controlling the speed of ammonia; the precursor is calcined at 200℃.The product is characterized by X-ray diffraction(XRD) and transmission electron microscopy(TEM),with purity of 100% and particle size around 20nm.
参考文献
| [1] | Pan'kov V V .Interaction of(MnZn)O solid solutions with Fe2O3 as intermediate stage of formation of Mn-Zn ferrites[J].Cerarm Int,1988,14(02):87. |
| [2] | 张国昀,姜长印,万春荣,何培炯.以Mn3O4为前驱体的LiMn2O4及其电化学性能[J].无机材料学报,2001(04):667-671. |
| [3] | 欧阳旭清,张光宇,曾育民.我国Mn3O4生产中存在的问题及其应对措施[J].金属材料与冶金工程,2007(02):8-13. |
| [4] | 王红太.国内四氧化三锰的生产工艺现状及发展方向[J].山西化工,2006(03):55-57. |
| [5] | 张三田.用原生锰矿石制取高纯四氧化三锰[J].中国锰业,2000(03):22-24. |
| [6] | 潘其经 .四氧化三锰的制备方法和发展前景[J].中国锰业,1998,16(03):51. |
| [7] | 董俊 .高品质Mn3O4粉末的制备[J].中国锰业,1995,13(03):21. |
| [8] | Sagheer A L;Hasan F A;Pasu puletv M A et al.Lowtemperature synthesis of nanominite Mn3O4[J].Journal of Materials Science Letters,1999,18(03):209. |
| [9] | Fritsch S.;Rousset A.;Kulkarni GU.;Sarrias J. .Low-temperature oxidation of Mn3O4 hausmannite[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,1998(8):1185-1194. |
| [10] | 陈权启,汤林.催化氧化法制备高比表面四氧化三锰[J].贵州化工,2002(04):11-13. |
| [11] | 薛娟琴,王成刚,刘小勇.以硫酸锰为原料制备四氧化三锰的理论分析[J].西安建筑科技大学学报（自然科学版）,2000(03):297-299. |
| [12] | 张西军,袁伟.一步水解氧化法制备纳米级Mn3O4[J].北京化工大学学报(自然科学版),2002(03):74-78. |
| [13] | 骆艳华,陈思学,王凡,王克玉.硫酸锰直接制备四氧化三锰的研究[J].矿业快报,2008(02):17-19. |
| [14] | 邹兴;孙宁磊;陈德胜.用硫酸锰溶液直接制备高纯四氧化三锰的难点和进展[A].北京:冶金工业出版社,2005:408. |
| [15] | 邹兴,孙宁磊,王国承.用空气直接氧化游离二价锰离子制备高纯四氧化三锰[J].北京科技大学学报,2007(12):1250-1253. |
| [16] | 徐滨士.纳米表面工程[M].北京:化学工业出版社,2003:9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%