The segregation and precipitation behavior of Alloy 690 containing 0.001-0.11 wt% nitrogen during isothermal solidification at 1370 and 1355 ℃ have been investigated using optical microscopy （OM）,electron probe microanalysis （EPMA） and transmission electron microscopy （TEM）.The results indicate that the volume fraction of TiN-type nitride formed during isothermal solidification increases with the nitrogen content of Alloy 690.Segregation of Ti and Cr exists in samples solidified at 1370 and 1355℃.The Ti content in the residual liquid markedly decreases and the concentration of Cr increases when the nitrogen content of Alloy 690 increases.Furthermore,N and S also show segregation to some extent in the residual liquids at 1355℃.Accompanying by the segregation of Cr,Ti,C,N and S,sulfides and chromium nitrides form.In a low nitrogen content Alloy 690,sulfur segregates and precipitates in the form of Ti 4 C 2 S 2 and （Cr,Ti）S,but in the form of （Cr,Ti）S or CrS in a high nitrogen content Alloy 690.（Cr,Ti）N-type nitrides with an fcc crystal structure have been identified in a sample with 0.11 wt% nitrogen.
参考文献
| [1] | A. Di Schino;J.M. Kenny .Grain refinement strengthening of a micro-crystalline high nitrogen austenitic stainless steel[J].Materials Letters,2003(12):1830-1834. |
| [2] | J.Kunze;C.Mickel .Precipitation of titanium nitride in low-alloyed steel during solidification[J].Steel Research,1997(9):403-408. |
| [3] | P.L. Ferrandini;C.T. Rios;A.T. Dutra .Solute segregation and microstructure of directionally solidified austenitic stainless steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(0):139-144. |
| [4] | Q. FENG;L.J. CARROLL;T.M. POLLOCK .Solidification Segregation in Ruthenium-Containing Nickel-Base Superalloys[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2006(6):1949-1962. |
| [5] | R.S. DUTTA;A. LOBO;R. PURANDARE .Corrosion Behavior of Austenitic Alloy 690 under Anodic and Cathodic Potentials[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2002(5):1437-1447. |
| [6] | R.S. Dutta;R. Tewari;P.K. De .Effects of heat-treatment on the extent of chromium depletion and caustic corrosion resistance of Alloy 690[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(2):303-318. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%