以纳米ATO(掺锑二氧化锡)浆料和纳米TiO2粉体配合高反射与高辐射性能的颜填料,制备了一种水性纳米复合隔热涂料.乳液、颜料和填料筛选实验表明,聚合物乳液种类对涂层隔热性能几乎没有影响;颜料中,金红石型二氧化钛是性能最好的反射填料,其用量在PVC=18%时,涂层隔热性能最好;绢云母具有一定的辐射隔热效果,当其质量分数为11%时,涂层性能最忧,辐射率可达0.86;纳米ATO浆料具有良好的隔热效果,其最佳用量为10%.当以质量比为1:2的添加量将纳米ATO和纳米TiO2加入到涂料中,所得涂层在全波段(200～2 500 nm)的太阳热反射比为86%,辐射率为0.86.
参考文献
| [1] | Ronnen Levinson;Hashem Akbari;Joseph C. Reilly .Cooler tile-roofed buildings with near-infrared-reflective non-white coatings[J].Building and environment,2007(7):2591-2605. |
| [2] | Levinson R;Berdahl P;Akbari H;Miller W;Joedicke I;Reilly J;Suzuki Y;Vondran M .Methods of creating solar-reflective nonwhite surfaces and their application to residential roofing materials[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2007(4):304-314. |
| [3] | A. Synnefa;M. Santamouris;I. Livada .A study of the thermal performance of reflective coatings for the urban environment[J].Solar Energy,2006(8):968-981. |
| [4] | 郭清泉,周立清,黄惠民,陈焕钦.金属用单涂层日光热反射水性涂料的研制[J].涂料工业,2006(06):5-7,10. |
| [5] | 马宏,刘文兴,孟军锋,董浩,王进忠,裴晓峥.高性能太阳热反射隔热涂层的研制[J].现代涂料与涂装,2006(07):55-56,60. |
| [6] | MIL-E-46136A.MIL-E-46136A Enamel,semi-gloss,alkyd,solar heat reflecting,olive drab[S].U.S.Government Printing Office,1976. |
| [7] | 殷燕子,林安,刘秀生,程学群.太阳热反射涂料的反射率检测方法研究及其数学模型[J].材料保护,2004(05):8-10. |
| [8] | 战为民,邓永青,李少春.日光热反射涂料的研究[J].现代涂料与涂装,2001(02):12-14. |
| [9] | 陈先;郭年华;李明 等.功能涂料太阳热反射率测试方法研究[J].化工新型材料,2000,28(02):36-38. |
| [10] | 郭声波,叶建军.反光隔热防水涂料的研究[J].新型建筑材料,2005(10):46-49. |
| [11] | 王建雄,王秋林.绢云母的特性及其对紫外线的屏蔽作用[J].湖南有色金属,2002(06):6-7,22. |
| [12] | 张贵军,陈中华,姜疆,余飞,曾幸荣.水性纳米掺锑二氧化锡（ATO）浆料的研制[J].电镀与涂饰,2009(08):47-51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%