利用固体废弃物磷石膏制备轻质墙体材料,实验研究了煅烧温度、水灰比和铝粉掺量对磷石膏试块的强度和轻质化的影响,通过扫描电镜（SEM）分析磷石膏试块内部和表面的结晶情况。实验结果显示：当煅烧温度为170℃、水灰比0.70、铝粉掺量0.02%的工艺下,磷石膏试块7d的抗压强度为4.6MPa,抗折强度为2.1MPa,体积密度为0.93g/cm3。
Lightweight mural materials were prepared from solid waste phosphogypsum.How the calcining temperature,water cement ratio(w/c) and admixture of aluminum influence the strength and weight-lightening of the lightweight mural material were discussed.SEM was used to observe the crystallization situation inside and outside the lightweight mural materials.Experimental results show that lightweight mural material has the compressive strength of 4.6MPa,the bending strength of 2.1MPa,and the density of 0.93g/cm3,when the lightweight mural material with w/c of 0.70 and 0.02% admixture of aluminum is calcined at 170℃ for 7days.
参考文献
| [1] | Singh M .Role of phosphogypsum impurities or strength and microstrucyure of selenite plaster[J].Constr Build Materi,2005,19(06):480-486. |
| [2] | 陶俊法.云南硫酸磷肥工业的发展方向[J].磷肥与复肥,2007(02):8-10,21. |
| [3] | 林倩,吴红,曹建新,刘毅.浇注成型法制磷石膏轻质墙体砖的研究[J].贵州工业大学学报（自然科学版）,2006(04):42-45. |
| [4] | 尹忠,陈馥,梁发书,王永玉.泡沫评价及发泡剂复配的实验研究[J].西南石油学院学报,2004(04):56-58. |
| [5] | 杜采颐,严云,胡志华,谢晓丽,王素娟.利用磷石膏制备轻质材料初探[J].建筑材料学报,2008(03):353-358. |
| [6] | 李建锡,余苏,马丽萍,舒艺周,唐霜露,卢凯芳,张平,曹盈盈.磷石膏预分解的热分析研究[J].环境工程学报,2009(10):1861-1864. |
| [7] | 余苏,李建锡,马丽萍,舒艺周,唐霜露,卢凯芳,张平,曹盈盈.磷石膏分解特性对磷石膏制硫酸联产水泥新工艺的影响研究[J].昆明理工大学学报（理工版）,2010(04):80-84. |
| [8] | 彭家惠,彭志辉,张建新,万体智.磷石膏中可溶磷形态、分布及其对性能影响机制的研究[J].硅酸盐学报,2000(04):309-313. |
| [9] | 刘代俊,刘玉琨,钟本和,王雪梅,胡厚美,杨三可,胡海,周永波.高强磷石膏建材的硬化机理[J].化工矿物与加工,2005(05):24-25,27. |
| [10] | 杨家宽,谢永中,刘万超,任婷艳,林显龙.磷石膏蒸压砖制备工艺及强度机理研究[J].建筑材料学报,2009(03):352-355. |
| [11] | 杨敏,钱觉时,王智,黄煜镔.杂质对磷石膏应用性能的影响[J].材料导报,2007(06):104-106. |
| [12] | SINGH M;GARG M;VERMA C L et al.An improved process for the purification of phosphogypsum[J].Construction and Building Materials,1996,10(08):597-600. |
| [13] | Nurhayat Degirmenci .Utilization of phosphogypsum as raw and calcined material in manufacturing of building products[J].Construction and Building Materials,2008(8):1857-1862. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%