研究了环氧树脂/丁腈橡胶(EP/A)并用体系和二月桂酸二丁基锡(B)对氰酸酯树脂(CE)的固化以及CE/EP/A膜性能的影响.室温下停放30 d的CE/EP/A/B体系能有效固化.A用量从20%提高到24%,CE/EP/A/B(95-x/5/x/0.14)体系固化温度从163.9℃下降到152.2℃;B用量从0.14%增加到0.3%,CE/EP/A/B(75/5/20/v)体系固化温度从163.9℃下降到148.9℃.A用量从20%增加到25%,CE/EP/A/B(95-x/5/x/0.06)膜冲击强度和柔韧性分别从43kg·cm和15 mm提高到50 kg·cm和10 mm,热分解温度从394.4℃下降到377.2℃;B用量增加,CE/EP/A/B膜冲击强度和柔韧性下降,热稳定性提高.
参考文献
| [1] | Gomez CM;Recalde IB;Mondragon M .Kinetic parameters of a cyanate ester resin catalyzed with different proportions of nonylphenol and cobalt acetylacetonate catalyst[J].European Polymer Journal,2005(11):2734-2741. |
| [2] | Kissounko DA;Deitzel JM;Doherty SP;Shah A;Gillespie JW .Understanding the role of clay silicate nanoparticles with organic modifiers in thermal curing of cyanate ester resin[J].European Polymer Journal,2008(9):2807-2819. |
| [3] | 孟季茹,梁国正,赵磊.傅立叶红外光谱法研究氰酸酯树脂及其改性体系的固化反应[J].高分子材料科学与工程,2003(02):180-183. |
| [4] | Shi HH;Fang ZP;Gu AJ;Tong LF;Xu ZB .Carboxyl-terminated butadiene-acrylonitrile rubber modified cyanate ester resin[J].Journal of Applied Polymer Science,2007(5):3098-3104. |
| [5] | Minfeng Zeng;Xudong Sun;Yun Wang;Mingzhu Zhang;Yongmiao Shen;Baoyi Wang;Chenze Qi .A positron annihilation study on the microstructure of cyanate ester resin toughened by carboxyl-terminated butadiene-acrylonitrile rubber system[J].Polymers for advanced technologies,2008(11):1664-1671. |
| [6] | Suman JN;Kathi J;Tammishetti S .Thermoplastic modification of monomeric and partially polymerized Bisphenol A dicyanate ester[J].European Polymer Journal,2005(12):2963-2972. |
| [7] | Hahn T;Heimfarth JP;Roewer G;Kroke E .Silicon nano particles: Surface characterization, defects and electronic properties[J].Physica status solidi, B. Basic research,2008(5):959-962. |
| [8] | A. V. Sugonyako;A. A. Turkin;R. Gaynutdinov;D. I. Vainshtein;H. W. den Hartog;A. A. Bukharaev .Systematic UHV-AFM experiments on Na nano-particles and nano-structures in NaCl[J].Physica Status Solidi. C, Conferences and critical reviews,2005(1):289-293. |
| [9] | Yu DH;Wang B;Feng Y;Fang ZP .Investigation of free volume, interfacial, and toughening behavior for cyanate ester/bentonite nanocomposites by positron annihilation[J].Journal of Applied Polymer Science,2006(2):1509-1515. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%