采用丙烯酸改性多孔二氧化硅微粉为填料,以E-44环氧树脂为基体,乙二胺为固化剂制备出具有吸声性能的涂层,并对其耐磨性和吸声性能进行了测试.结果表明,涂层的耐磨性随着填料加入量的增加先增大后减小,填料含量为60％时磨损率最低；对于频率为1000Hz的声音,吸声系数随着填料的增加而增大,平均吸声系数可达0.22,同时,粒径小的填料吸声系数高于粒径大的填料吸声系数.
参考文献
| [1] | M. Vasina;D. C. Hughes;K. V. Horoshenkov;L. Lapcik Jr. .The acoustical properties of consolidated expanded clay granulates[J].Applied acoustics,2006(8):787-796. |
| [2] | Morgan P A;Wate S G R .A novel approach to the acoustic characterization of porous road surfaces[J].Applied Acoustics,2003,64(02):1171. |
| [3] | 张守梅,曾令可,张明,黄浪欢,王慧,程小苏.地铁多孔吸音材料的研制[J].新型建筑材料,2003(05):60-62. |
| [4] | T. Y. Lo;H. Z. Cui .Effect of porous lightweight aggregate on strength of concrete[J].Materials Letters,2004(6):916-919. |
| [5] | 奚新国;许仲梓.Study on sound adsorption porous concrete(吸声多孔混凝土的研究)[J].建筑材料学报,2001(01):86. |
| [6] | 黄学辉;曹雪枫 et al.Research on polypropylene fiber reinforced cement-based sound-absorbing materials(聚内烯纤维增强的水泥基吸声材料的研制)[J].武汉理工大学学报,2004,28(04):530. |
| [7] | 杜功焕;朱哲民;龚秀芬.声学基础-下册[M].南京:南京大学出版社,1981:180. |
| [8] | Li Yan;Hu Yanping;Hu Chunjing .Microstructures and mechanical properties of natural fibers[J].Advances in Materials Research,2008,33-37:553. |
| [9] | 陈艳;蔡忠龙.Polyimide/silica nano-scale composites(聚酰亚胺/二氧化硅纳米尺度复合材料的研究)[J].高分子学报,1997(01):73. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%