采用水热法制备了CdSe纳米棒,并用TEM、SEM、XRD、TGA-DTA对其进行了表征.结果表明,纳米棒直径在100nm左右,长度约300nm;纳米棒具有闪锌矿的结构;将CdSe纳米棒均匀涂在导电玻璃的导电面上,在400℃下煅烧30min后制备成纳米棒膜电极,并进行了光电化学研究,纳米棒膜结构电极最高单色光的光电转换效率(IPCE)可达74%.
参考文献
| [1] | 姜月顺;李铁津.光化学[M].北京:化学工业出版社,2005 |
| [2] | 马娟,陈秀梅,李邨.聚苯乙烯为模板制备CdSe纳米粒子[J].南京师大学报(自然科学版),2004(02):61-62. |
| [3] | Li YD.;Ding Y.;Qian YT.;Yang L.;Zhou GE.;Liao HW. .Nonaqueous synthesis of CdS nanorod semiconductor[J].Chemistry of Materials,1998(9):2301-2303. |
| [4] | Wang W Z;Geng Y;Yan P et al.[J].Inorganic Chemistry Communications,1999,2:83-85. |
| [5] | Yu SH.;Yang J.;Han ZH.;Xie Y.;Qian YT.;Liu XM.;Wu YS. .A novel solventothermal synthetic route to nanocrystalline CdE (E = S, Se, Te) and morphological control[J].Chemistry of Materials,1998(9):2309-2312. |
| [6] | Xu D S;Shi X S .[J].Journal of Physical Chemistry,2000,104(21):5061-5063. |
| [7] | Trindade T;O' Brien P et al.[J].J Mate Chem,1996,6(03):343-347. |
| [8] | Huynh W U;Peng X G;Alivisatos A P.[J].Adv func Mat,1999(11):923. |
| [9] | Qing P;Dong Y J;Deng Z X et al.[J].Inorganic Chemistry,2002,41:5249-5254. |
| [10] | Nazeeruddin M K;Kay A;Rodicio I et al.[J].Journal of the American Chemical Society,1993,115:6382-6390. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%