SCC of XT0 and Its Deteriorated Microstructure in Simulated Acid Soil Environment

材料科学技术（英文）, 2009, 25(2): 169-174.

^1, , ^2, , ^3, , ^4,

1.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China

2.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China

3.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China

4.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China

SCC of XT0 and Its Deteriorated Microstructure in Simulated Acid Soil Environment

Zhiyong Liu ^1, , Guoli Zhai ^2, , Xiaogang Li ^3, , Cuiwei Du ^4,

1.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China

2.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China

3.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China

4.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China

Keywords： X70 steel

In order to study the stress corrosion cracking (SCC) of X70 pipeline steel and its weld joint in acid soil environment of southeast of China, two simulating methods were used here. The one was to obtain the bad microstructures in heat affected zone by annealing at 1300℃ for 10 min and air cooling to room temperature,the other was to get a series of simulating solutions of the acid soil environment. SCC susceptibilities of X70pipeline steels'before and after being normalized in the simulated solutions were studied by slow strain rate test (SSRT) and microstructural observation of fracture areas. Potentiodynamic polarization curves were used to study the electrochemical behaviour of different microstructures. SCC does occur to both the as-received material and normalized microstructure after heat treatment as the polarization potential decreased. Hydrogen embrittlement (HE) is indicated occurring to all tested materials at -850 mV (vs SCE) and -1200 mV(vs SCE). The SCC mechanisms are different within varying potential range. Anodic dissolution is the key cause as polarization potential higher than null current potential, and HE will play a more important role as polarization potential lower than the null current potential.

参考文献

[1]	C. Manfredi;J.L. Oteguj .Failures by SCC in buried pipelines[J].Engineering failure analysis,2002(5):495-509.
[2]	R.N. Parkins .Mechanistic Aspects of Intergranular Stress Corrosion Cracking of Ferritic Steels[J].Corrosion: The Journal of Science and Engineering,1996(5):363-374.
[3]	J.Q. Wang;A. Atrens .SCC initiation for X65 pipeline steel in the "high" pH carbonate/bicarbonate solution[J].Corrosion Science,2003(10):2199-2217.
[4]	L. J. Qiao;J. L. Luo;X. Mao .Hydrogen evolution and enrichment around stress corrosion crack tips of pipeline steels in dilute bicarbonate solution[J].Corrosion: The Journal of Science and Engineering,1998(2):115-120.
[5]	S.-H. Wang;W. Chen;F. King .Precyclic-Loading-Induced Stress Corrosion Cracking of Pipeline Steels in a Near-Neutral-pH Soil Environment[J].Corrosion: The Journal of Science and Engineering,2002(6):526-534.
[6]	D.X. He;W. Chen;J.L. Luo .Effect of Cathodic Potential on Hydrogen Content in a Pipeline Steel Exposed to NS4 Near-Neutral pH Soil Solution[J].Corrosion: The Journal of Science and Engineering,2004(8):778-786.
[7]	L.Niu;Y.F.Cheng .[J].Applied Surface Science,2007,7:1.
[8]	G. Van Boven;W. Chen;R. Rogge .The role of residual stress in neutral pH stress corrosion cracking of pipeline steels. Part I: Pitting and cracking occurrence[J].Acta materialia,2007(26):29-42.
[9]	W. Chen;G. Van Boven;R. Rogge .The role of residual stress in neutral pH stress corrosion cracking of pipeline steels - Part II: Crack dormancy[J].Acta materialia,2007(26):43-53.
[10]	H. Asahi;T. Kushida;M. Kimura;H. Fukai;S. Okano .Role of microstructures on stress corrosion cracking of pipeline steels in carbonate-bicarbonate solution[J].Corrosion: The Journal of Science and Engineering,1999(7):644-652.
[11]	J.Bulger;J.Luo.[A].,2000:947.
[12]	J.G. Gonzalez-Rodriguez;M. Casales;V.M. Salinas-Bravo .Effect of Microstructure on the Stress Corrosion Cracking of X-80 Pipeline Steel in Diluted Sodium Bicarbonate Solutions[J].Corrosion: The Journal of Science and Engineering,2002(7):584-590.
[13]	R. Chu;W. Chen;S. -H. Wang .Microstructure Dependence of Stress Corrosion Cracking Initiation in X-65 Pipeline Steel Exposed to a Near-Neutral pH Soil Environment[J].Corrosion: The Journal of Science and Engineering,2004(3):275-283.
[14]	S.A.Serebrinsky;G.S.Duff;J.R.Galvele .[J].Corrosion Science,1999,41(11):191.
[15]	W. CHEN;F. KING;T.R. JACK .Environmental Aspects of Near-Neutral pH Stress Corrosion Cracking of Pipeline Steel[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2002(5):1429-1436.
[16]	X.Liu;X.Mao .[J].Scripta Materialia,1995,33(13):145.
[17]	S.Lee;B.C.Kim;D.Kwon .[J].Metallurgical and Materials Transactions,1992,23A:2803.
[18]	R.N.Parkins .[J].Corrosion Science,1980,20(02):147.
[19]	B. Gu;W. Z. Yu;J. L. Luo;X. Mao .Transgranular stress corrosion cracking of X-80 and X-52 pipeline steels in dilute aqueous solution with near-neutral pH[J].Corrosion: The Journal of Science and Engineering,1999(3):312-318.
[20]	S. Nesic;J. Postlethwaite;S. Olsen .An Electrochemical Model for Prediction of Corrosion of Mild Steel in Aqueous Carbon Dioxide Solutions[J].Corrosion: The Journal of Science and Engineering,1996(4):280-294.
[21]	B. Gu;J. Luo;X. Mao .Hydrogen-facilitated anodic dissolution-type stress corrosion cracking of pipeline steels in near-neutral pH solution[J].Corrosion: The Journal of Science and Engineering,1999(1):96-106.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

SCC of XT0 and Its Deteriorated Microstructure in Simulated Acid Soil Environment

参考文献