对比了搅拌、滚磨、行星球磨三种混料方法的分散效果,研究了行星球磨工艺对注凝成型超细氧化锆陶瓷(D50=0.19 μm)浆料流变性以及对生坯和陶瓷性能的影响,分析了"过磨"浆料粘度增加的原因.结果表明:行星球磨制备的浆料粘度更低,在200 r/ min球磨4 h,同相量为50 vol%的浆料起始粘度仪为0.289 Pa·s;颗粒变细是"过磨"浆料粘度增加的主要原因,可通过加入少量分散剂来降低浆料的粘度;适当延长球磨时间,生坯及陶瓷性能均有所提高,球磨12 h制备的陶瓷平均强度达960 MPa,韧性高达17.3 MPa·m1/2.
参考文献
| [1] | 黄勇,张立明,杨金龙,谢志鹏,汪长安,陈瑞峰.先进陶瓷胶态成型新工艺的研究进展[J].硅酸盐学报,2007(02):129-136. |
| [2] | Janney M A .Method for Molding Ceramic Powders[P].US,C03B19/12,US4894194,1990-01-16. |
| [3] | Janney M A;Omatete O O .Method for Molding Ceramic Powders Using a Water-based Gel-casting[P].US,C04B35/634,US5028362,1991-07-02. |
| [4] | Janney M A;Omatete O O .Method for Molding Ceramic Powders Using a Water-based Gel-casting Process[P].US,C03B19/12,US5145908,1992-09-8. |
| [5] | Omatete O O;Janney M A;Strcklow R A .Gelcasting-a New Ceramic Forming Process[J].American Ceramic Society Bulletin,1991,70(10):1641-1649. |
| [6] | Young A C;Omatete O O;Janncy M A et al.Gelcasting of Alumina[J].Journal of the American Ceramic Society,1991,74(03):612-618. |
| [7] | 焦宝祥 .注凝成型制备高性能氧化铝-氧化锆复相陶瓷[D].南京:南京工业大学,2004. |
| [8] | Ewais E;Zaman A A;Sigmund W .Temperature Induced Forming of Zirconia from Aqueous Slurries:Mechanism and Rheology[J].Journal of the European Ceramic Society,2002,22(16):2805-2812. |
| [9] | 王金锋,高雅春,谢志鹏,孙加林.pH值对ZrO2超细粉体料浆性能的影响[J].人工晶体学报,2007(01):70-75. |
| [10] | 杨金龙,谢志鹏,汤强,黄勇.α-Al2O3悬浮体的流变性及凝胶注模成型工艺的研究[J].硅酸盐学报,1998(01):41-46. |
| [11] | 孙静,孙伟燕,高濂.聚丙烯酸铵在纳米Y-TZP上的定量吸附研究[J].无机材料学报,1999(04):645. |
| [12] | 王金锋,高雅春,谢志鹏,孙加林.注凝成型超细二氧化锆悬浮体的制备[J].材料工程,2008(03):18-21,27. |
| [13] | 梁开明;顾扣芬;顺守仁 等.ZTA陶瓷ZrO2的韧化机制与断裂特征[J].硅酸盐学报,1995,20(05):477-487. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%