通过溶液法制备羟基磷灰石粉体,研究了反应体系与分散剂、溶液浓度、反应温度、pH值和陈化时间等工艺因素对羟基磷灰石粉体粒度和形貌的影响.研究表明,高浓度(1mol/L)乙醇-水溶液条件下,也可通过控制工艺因素获得不同形态(如颗粒状、针状)的羟基磷灰石粉体.粉体煅烧可得仅含羟基磷灰石和磷酸钙的生物陶瓷粉.提高pH值、延长陈化时间可以提高煅烧产物中羟基磷灰石的含量.
参考文献
| [1] | Suchhanek W;Yoshimura M .Processing and properties of hydroxyapatite-based biomaterials for use as hard tissue replacement implants[J].Journal of Materials Research,1998,13:94. |
| [2] | 靳正国,王英,郭多力,郭庆捷.超声波处理对羟基磷灰石结晶形貌的影响[J].硅酸盐学报,2003(06):608-611. |
| [3] | 李蔚,高濂.纳米羟基磷灰石粉体的制备和低温烧结[J].过程工程学报,2002(04):305-308. |
| [4] | Ishikawe K;Ducheyne P;Radin S.Determination of Ca/P ratio in calcium-deficient hydroxyapatite using X-ray diffraction analysis[J].Journal of Materials Science:Materials in Medicine,1993(04):165. |
| [5] | Li YuBao.Morphology and composite of nanograde calcium phosphate needle-like crystals fored by simple hydrothermal treatment[J].Journal of Materials Science:Materials in Medicine,1994(05):326. |
| [6] | 吕奎龙,周玉,孟祥才,李星逸,滕立群.工艺因素对纳米羟基磷灰石结晶形态的影响[J].材料科学与工艺,2003(03):254-257. |
| [7] | 宋云京,李木森,温树林,宿庆才,姜庆辉.浓度、温度和陈化对羟基磷灰石合成的影响[J].机械工程材料,2003(05):19-21. |
| [8] | 许艳慧,李志安,李四群.纳米羟基磷灰石复合材料的研究（Ⅰ）合成因素对纳米羟基磷灰石生成的影响[J].口腔医学研究,2002(06):367-369. |
| [9] | Knepper M.;Milthorpe BK.;Moricca S. .STABILITY OF HYDROXYAPATITE WHILE PROCESSING SHORT-FIBRE REINFORCED HYDROXYAPATITE CERAMICS[J].Biomaterials,1997(23):1523-1529. |
| [10] | 憨勇,徐可为.针状缺钙羟基磷灰石涂层的烧结特征及磷酸氢钙相的影响[J].硅酸盐学报,1998(04):458-464. |
| [11] | 储成林;林景川;尹钟大 等.羟基磷灰石(HA)生物复合材料的研究进展[J].材料导报,1999,13(02):51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%