采用柠檬酸 Sol-gel工艺合成了 BaFe12O19/SiO2微晶玻璃陶瓷,并对其介电常数及其磁导率在100MHz~6GHz下的变化规律进行了研究.结果表明,BaFe12O19/SiO2微晶玻璃陶瓷的合成与体系中 Fe/Ba、烧结温度密切相关;其介电常数、磁导率基本都随测试频率的增加而下降;介电损耗值最大达到0.40,磁损耗值较小.
BaFe12O19/SiO2 microcrystallite glass ceramics were prepared by citrate so1-gel pro- cess; The complex dielectric constant and complex permeability dispersion were investigated in 100MHz-6GHz range. The results obtained show those conditions such as Ba/Fe, sintering tem- perature have a close effect on the synthesis of BaFe12O19/SiO2 microcrystallite glass ceramics; the complex dielectric constant and complex permeability will decrease as the measuring frequency increasing, and maximum dielectric loss is 0.40, but magnetic loss nearoy zero.
参考文献
[1] | Sǖrig C, Hempel K A, Bonnenberg D. Appl. Phys. Lett., 1993, 63 (20): 2836--2838. [2] Pullar R C, Taylor M D, Bhattacharya A K. J. Mat. Sci., 1997, 32: 349--352. [3] Sǖrig C, Hempel K A, Bonnenberg D. IEEE Trans. Magn., 1994, 30 (6): 4092--4094. [4] Chung-kook L, Yolande B, Robert F. J. Am. Ceram. Soc., 1996, 79 (1): 183--192. [5] Klupsch Th, Steinbeiss E, Mǖller R. J. Mag. Magn. Mat., 1999, 196-197: 264--265. [6] K Lee C, Speyer R F. J. Mat. Sci., 1994, 29: 1348--1351. [7] Mǖller R, Ulbrich C, Schǖppel W. J. Eur. Ceram. Soc., 1999, 19: 1547--1550. [8] Wei Zhong, Weiping Ding, Yumei Jiang. J. Am. Ceram. Soc., 1997, 80 (12): 3258--3262. [9] P.W.麦克米伦著,王仞千译. 微晶玻璃. 北京: 中国建筑工业出版?社,1988. [10] 崔茂林, 等. 玻璃工艺学. 北京: 轻工业出版社,1982. [11] 张有纲, 黄永杰, 罗迪民. 磁性材料. 成都:成都电讯工程学院出版社,1988. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%