研究了氯丁橡胶和氯磺化聚乙烯(CR/CSM)不同并用比共混胶的力学性能,以及并用胶经150℃不同浓度的氢氧化钠、盐酸溶液浸泡24h后的性能变化与机理.对比温度下胶片经酸碱溶液浸泡后的质量变化、拉伸强度变化、扫描电镜图以及红外谱图.结果表明,当CR/CSM质量比为80/20时并用胶表现出较好的力学性能,且交联密度较大.150℃条件下,在40％的氢氧化钠溶液中浸泡24h后,CR/CSM质量比为80/20的并用胶的拉伸强度保持率最高,质量变化率较小,表现出较好的耐碱性能.150℃条件下,在5％的盐酸溶液中浸泡24h后,CR/CSM质量比为20/80的并用胶的拉伸强度保持率最高,质量变化率较小,表现出较好的耐酸性能.氯丁橡胶和氯磺化聚乙烯(CR/CSM)的不同并用比决定了共混胶耐高温酸碱性能.
参考文献
| [1] | Chih-Wei Lin;Chi-Hui Chien;Jinzhu Tan;Yuh J.Chao;J.W. Van Zee .Chemical degradation of five elastomeric seal materials in a simulated and an accelerated PEM fuel cell environment[J].Journal of Power Sources,2011(4):1955-1966. |
| [2] | Mitra S;Ghanbari-Siahkali A;Kingshott P;Rehmeier HK;Abildgaard H;Almdal K .Chemical degradation of crosslinked ethylene-propylene-diene rubber in an acidic environment. Part I. Effect on accelerated sulphur crosslinks[J].Polymer Degradation and Stability,2006(1):69-80. |
| [3] | Mitra, S;Ghanbari-Siahkali, A;Almdal, K .A novel method for monitoring chemical degradation of crosslinked rubber by stress relaxation under tension[J].Polymer Degradation and Stability,2006(10):2520-2526. |
| [4] | 陈焜盛,罗权焜.影响氯磺化聚乙烯/丁腈橡胶共混物耐热老化性能的因素[J].合成橡胶工业,2006(05):360-363. |
| [5] | 高树峰,宗成中,方鹏.EPDM的性能研究[J].橡塑技术与装备,2005(04):32-35. |
| [6] | 殷以华,董慧,季兴敏,李国辉,姜建平,郑化.羧甲基纤维素与丙烯酸接枝共聚凝胶的溶胀动力学及过溶胀平衡特性的研究[J].化学学报,2007(03):271-278. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%