分析了结晶器液面波动、结晶器锥度、结晶器冷却制度、连铸保护渣、二冷制度等连铸工艺对低合金钢板坯角部横裂纹缺陷的影响,在此基础上,提出了改善板坯角部横裂纹的有效措施,即稳定结晶器液面、优化结晶器锥度、弱化结晶器冷却和连铸二次冷却,改进连铸保护渣等.研究结果经实施应用,明显减轻了板坯角部横裂纹缺陷,消除了因低合金高强度钢连铸坯角部横裂纹缺陷引起的热轧板卷边裂缺陷.
参考文献
| [1] | Suzuki H G;Nishimura S;Imamura J.Embrittlement of Steels Occurring in the Temperature Range from 1 000 ℃ to 600 ℃[J].Transaction of the Iron and Steel Institute of Japan,1984(24):169-177. |
| [2] | Turkdogan E T.Causes and Effects of Nitride and Carbonitride Precipitation in HSLA Steels in Relation to Continuous Casting[J].Steelmaking Conference Proceedings,1987(70):399-409. |
| [3] | Nozaki T;Matsuno J;Murata K.A Secondary Cooling Pattern for Preventing Surface Cracks of Continuous Casting Slab[J].Transaction of the Iron and Steel Institute of Japan,1978(20):330-338. |
| [4] | 职建军.宝钢连铸板坯角横裂缺陷的改善[J].钢铁,2001(01):22-24. |
| [5] | 蔡开科;程士富.连续铸钢原理与工艺[M].北京:冶金工业出版社,1994:320-324. |
| [6] | Crowther D N;付万希;欧武昌 .微合金化元素对连铸裂纹的影响[J].钢铁钒钛,2002,23(01):64-80. |
| [7] | Hannerz N E .Critical Hot Plasticity and Transverse Cracking in Continuous Slab Casting with Particular Reference to Composition[J].Transactions of the Iron and Steel Institute of Japan,1985,25(01):149-158. |
| [8] | Mintz B;Abushosha R .Influence of Vanadium on Hot Ductility of Steel[J].Ironmaking and Steelmaking,1993,20(06):445-452. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%