以商品化软件PROCAST为基础进行二次开发, 对A356铝合金托盘件凝固过程显微疏松缺陷和二次臂距(SDAS)进行了数值分析, 建立了有氢气析出量影响在内的显微疏松判据模型, 预测了显微疏松出现的位置与体积分数. 预测结果得到了X射线无损探伤实验的验证. 开发了温度场测试系统, 测试了铸件凝固过程的冷却曲线, 模拟结果与实际结果符合良好.
参考文献
| [1] | Lessiter M J.Modeling workshop unveils deeper concerns[J].Modern Casting,1992(07):47. |
| [2] | Sutton T L.Aluminum casting-A step forward into the next century[J].Foundryman,1997(06):217-229. |
| [3] | Zhou J;Shivkumar S;Apelian D .Modeling of microstructure evolution and micro-porosity formation in cast aluminum alloys[J].AFS Transactions,1990,98:897-904. |
| [4] | Fang Q T;Granger D A .Porosity formation in modified and unmodified A356 alloy casting[J].AFS Transactions,1989,97:989-1000. |
| [5] | Atkin M R .Computerised method-calculation of feeder heat sizes by computer[J].Foundry Trade Journal,1981,151:184-190. |
| [6] | Atwood R C;Lee P D.A combined cellular automaton and diffusion model for the prediction of porosity formation during solidification[A].Aachen,Germany,2000:2-10. |
| [7] | Niyama E;Uchida T;Saito S .Predicting shrinkage in large steel casting from temperature gradient calculations[J].Cast Metals,1981,6:16-22. |
| [8] | Kao S T;Chang E .Feeding efficiency criteria for porosity formation in A356 alloy sand castings[J].AFS Transactions,1996,10(04):545-549. |
| [9] | Lee Y W;Chang E;Chieu C F .Modeling of feeder behaviour of solidifying Al-7Si-0.3Mg alloy plate castings[J].Metallurgical and Materials Transactions,1990,21:715-722. |
| [10] | Pequet C H;Rappaz M.Modeling of porosity formation during the solidification of aluminium alloys using a mushy zone refinement method[A].Aachen,Germany,2000:71-79. |
| [11] | Wendt J;Arola R;Verho M.A criterion for porosity formation in steel castings[A].Aachen,Germany,2000:110-117. |
| [12] | Chiesa F;Mammen J;Smiley L F .[J].AFS Transactions,1998,98-68:149. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%