以竹节为原料，采用磷酸法制备醋酸乙烯催化剂载体活性炭。采用N2吸附等温线、Boehm滴定法、热重-质谱仪( TG-MS)、傅里叶红外光谱仪( FT-IR)和扫描电子显微镜( SEM)，对磷酸法竹活性炭和水蒸气法椰壳活性炭的吸附性能、比表面积、孔结构、表面官能团和微观结构进行比较。结果表明，竹活性炭的醋酸吸附性能、比表面积和孔隙结构与椰壳活性炭相近；且竹活性炭具有更丰富的-COO-、-OH-和 P=O 、P-O-C和 P=OOH 等表面官能团。磷酸法竹活性炭的制备有望为醋酸乙烯催化剂载体活性炭的生产提供新工艺，实现对水蒸气法制备椰壳活性炭的替代。
Activated carbons were prepared from bamboo by phosphoric acid activation. Samples were characterized by N2 ad-sorption, Boehm titration, gas chromatograph-mass spectrometry, Fourier transform infrared spectroscopy and scanning electron mi-croscopy. The adsorption capacity,specific surface area, pore structure, surface functional groups and microstructure of the bamboo-based activated carbon were compared with those of coconut shell-based activated carbon prepared by steam activation. Results showed that both activated carbons had almost similar acetate adsorption capacities, specific surface area and pore structure. Besides, the bamboo-based activated carbon had many more carboxyl, phenolic hydroxyl, P=O , P-O-C and P==OOH groups than the coconut shell-based activated carbon.
参考文献
| [1] | 吴新华.载体活性炭的研制（I）-松根炭制维尼纶载体炭[J].福建林学院学报,1993(02):125. |
| [2] | 吴新华,余玮.载体活性炭的研究（Ⅱ）白炭制维尼纶载体炭[J].福建林学院学报,1993(04):365. |
| [3] | 于政锡,徐建本,郑起,林性贻,詹瑛瑛.活性炭载体对醋酸乙烯合成催化剂活性的影响[J].石油化工,2006(12):1140-1144. |
| [4] | 于政锡 .乙炔气相法合成醋酸乙烯催化剂的研究[D].福州:福州大学,2006. |
| [5] | 周桂林,蒋毅,吕绍洁,李子健,邱发礼.Zn（Ac）2/超高比表面积活性炭催化剂上乙炔法合成醋酸乙烯宏观动力学[J].燃料化学学报,2005(02):235-240. |
| [6] | 周桂林,蒋毅,吕绍洁,李子健,邱发礼.高比表面积活性炭载体结构对乙炔法合成醋酸乙烯催化剂活性的影响[J].石油化工,2004(07):608-611. |
| [7] | Kloubek J;Medek J .Porous structure of impregnated active car-bons and its significance for the catalytical activity[J].CARBON,1986,24(04):501-508. |
| [8] | Kawaguchi T;Nakagawa J;Wakasugi T .Method of preparation of an activated carbon supported zinc acetate catalyst[J].Applied Catalysis,1987,32(1-2):23-36. |
| [9] | Kawaguchi T;Wakasugi T .Activity and deactivation of a catalyst for vinyl acetate synthesis in an industrial fluidized reactor[J].Applied Catalysis,1988,36(1-2):67-79. |
| [10] | Boehm H P .Some aspects of the surface chemistry of carbon blacks and other carbons[J].CARBON,1994,32(05):759769. |
| [11] | Zhonghua Hu;M.P.Srinivasan;Yaming Ni .Novel activation process for preparing highly microporous and mesoporous activated carbons[J].Carbon: An International Journal Sponsored by the American Carbon Society,2001(6):877-886. |
| [12] | Arriagada R;García R;Molina-Sabio M et al.Effect of steam activation on the porosity and chemical nature of activated car-bons from Eucalyptus globules and peach stones[J].micro-porous materials,1997,8:123-130. |
| [13] | 林冠烽.炭化工艺对高活性木炭性能的影响[J].林业科学,2009(04):112-116. |
| [14] | 林冠烽,程捷,黄彪,杨建华,吴新华.高活性木炭的制备与孔结构表征[J].化工进展,2007(07):995-998. |
| [15] | Guo, YP;Rockstraw, DA .Activated carbons prepared from rice hull by one-step phosphoric acid activation[J].Microporous and Mesoporous Materials,2007(1/3):12-19. |
| [16] | A.M.Puziy;O.I.Poddubnaya;A.Martinez-Alonso;F.Suarez-Garcoa;J.M.D.Tascon;F.Suarez-Garcoa;J.M.D.Tascon .Synthetic carbons activated with phosphoric acid I. Surface chemistry and ion binding properties[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(9):1493-1505. |
| [17] | Solum MS.;Jagtoyen M.;Derbyshire F.;Pugmire RJ. .EVOLUTION OF CARBON STRUCTURE IN CHEMICALLY ACTIVATED WOOD[J].Carbon: An International Journal Sponsored by the American Carbon Society,1995(9):1247-1254. |
| [18] | Figueiredo J L;Pereira M F R;Freitas M M A et al.Modifica-tion of the surface chemistry of activated carbons[J].CARBON,1999,37(09):l379-l389. |
| [19] | Sangwichien C.;Aranovich GL.;Donohue MD. .Density functional theory predictions of adsorption isotherms with hysteresis loops[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2002(1/3):313-320. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%