为改善铸态WE43镁合金的成形加工性能,对钢模铸坯试样进行了均匀化退火处理,通过组织观察和维氏硬度测试,分析了不同均匀化退火温度和时间对合金组织和显微硬度的影响.通过拉伸试验测定了其退火后的力学性能,并用SEM观察了断口形貌.结果表明,最优的均匀化退火制度为440℃× 18h;在该工艺下均匀化退火后,合金表现出了较好的塑性.
参考文献
| [1] | 金军兵,王智祥,刘雪峰,谢建新.均匀化处理对AZ91镁合金组织和力学性能的影响[J].金属学报,2006(10):1014-1018. |
| [2] | P. J. Apps;H. Karimzadeh;J. F. King;G. W. Lorimer .Phase compositions in magnesium-rare earth alloys containing yttrium, gadolinium or dysprosium[J].Scripta materialia,2003(5):475-481. |
| [3] | 陈振华;严红革;陈吉华.镁合金[M].北京:化学工业出版社,2004 |
| [4] | Kleiner S;Beffort O;Uggowitzer P J .Micrestructure evolution during reheating of an extruded Mg-A1-Zn alloy into the semisolid state[J].Scripta Materialia,2004,51:405-410. |
| [5] | L. Cizek;M. Greger;L. Pawlica .Study of selected properties of magnesium alloy AZ91 after heat treatment and forming[J].Journal of Materials Processing Technology,2004(0):466-471. |
| [6] | Sarin Ignat;Pierre Sallamand;Dominique Grevey et al.Magnesium alloys (WE43 and ZE41) characterization for laser applications[J].Applied Surface Science,2004,233:382-391. |
| [7] | 黎文献.镁及镁合金[M].长沙:中南大学出版社,2005 |
| [8] | 李艳,刘奎立,陈芳雷.AZ31镁合金铸态组织及其退火工艺研究[J].锻压装备与制造技术,2006(03):67-69. |
| [9] | 郭强,严红革,陈振华,吴有伍.均匀化退火工艺对铸态AZ80镁合金组织与性能的影响[J].金属热处理,2006(07):77-80. |
| [10] | 彭建,张丁非,杨椿楣,丁培道.ZK60镁合金铸坯均匀化退火研究[J].材料工程,2004(08):32-35,53. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%