通过X射线衍射及磁测量手段研究了ErFe10.5-xCrxMo1.5(x=0、0.5、1、1.5、2、2.5、3)化合物的结构与居里温度.研究结果表明,ErFe10.5-xCrxMo1.5化合物均为ThMn12型结构.Cr对Fe的替代导致单胞体积V和晶格参数a,c均呈现先减后增的变化趋势,这可能与Cr的择优占位有关.对磁性质的研究结果表明,随着Cr替代量x的增加,ErFe10.5-xCrxMo1.5化合物的居里温度单调下降,这可能是Cr替代引起3d次晶格中铁磁交换作用削弱和Cr择优占位共同作用的结果.
参考文献
| [1] | Buschow K H J .[J].Journal of Magnetism and Magnetic Materials,1991,100:78-89. |
| [2] | Kamarád J;García-Landa R;Mikulina O et al.[J].Journal of Magnetism and Magnetic Materials,2001,226-230:1446-1448. |
| [3] | Garcia-Landa R;Tomey E;Fruchart D et al.[J].Journal of Magnetism and Magnetic Materials,1996,157/158:21-22. |
| [4] | Tomey E;Bacmann M;Fruchart D et al.[J].Journal of Alloys and Compounds,1995,231:195-200. |
| [5] | Tomey E;Bacmann M;Fruchart D et al.[J].Journal of Magnetism and Magnetic Materials,1996,157/158:115-116. |
| [6] | Moze O;Buschow K H J .[J].Journal of Alloys and Compounds,1996,233:165-168. |
| [7] | Moze O;Ibberson R M;Buschow K H J .[J].Solid State Communications,1991,78(05):473-476. |
| [8] | Chang C W;Yeh C C;Chang H W et al.[J].Journal of Applied Physics,2008,103(07):3021-3023. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%